杭钢高线（Hangzhou Iron and steel wire）.doc

杭钢高线（Hangzhou Iron and steel wire） All 52 pounds in February 2004 the first phase Brief introduction of Hangzhou high speed wire Stelmor controlled cooling system Hanjianfang (Hangzhou Iron And Steel Group Co of high-speed wire Co. Ltd. Hangzhou 310022) Abstract: This paper introduces the Stelmor cooling system of high speed wire rod Co. Ltd. Hangzhou Iron and steel structure, equipment, and the cooling process and form Effect. Key words: controlled cooling; temperature; cooling rate; microstructure U IJ swallow Stelmor cooling work control of high speed wire rod Co. Ltd. Hangzhou Art is provided by the Morgan Construction Company in the United States, which is the process of the hot rolled wire Material by slow cooling or rapid cooling of two modes to achieve the following goals: a The microstructure was uniform; for different steel grades, which may be the Mechanical properties of products, save after intermediate annealing process is, Fire; reduce the scale, improve the yield, reduce acid elimination Consumption, improve descaling characteristics, reduce working procedure cost. 1 cooling equipment The Stelmor cooling control system includes the following: No twist mill before the water tank; - no twist rolling mill cooling guide; - tank between twist free mill and reducing sizing unit; Reduction tank between sizing machine and spinning machine; - pinch roll; - spinning machine; Stelmor controlled cooling - transport line; - drum set. Specific arrangement as shown in figure 1. 1.1 cooling water tank The water tank for Stelmor controlled cooling line before the fall A low rolling temperature, rolling temperature control to achieve, and ultimately improve the production 1. charging table 2. weighing, measuring platform 3. heating furnace 4. high pressure water descaling machine 5 roller 6.1 ~ 6 insulation roughing mill No. 7.1 flying 8.6 ~ 12 mill frame No. 9.2 flying 10.13 mill l1. pinch roll, No. 3 flying, side loop 12. twist free mill (NTM) No. 13.2, No. 3 tank 1