pp塑料介绍（Introduction to PP plastics）.docVIP

pp塑料介绍（Introduction to PP plastics） PP plastic Polypropylene (PP) is a kind of fine resin developed after nylon. It is a kind of linear polymer with high density, no side chain and high crystallinity. It has excellent comprehensive properties. Not colored, white, translucent, waxy, lighter than polyethylene. Transparency is also better than polyethylene, more rigid than polyethylene. Name in Chinese (polypropylene) [1] English name: Polypropylene edits this paragraph PP plastic concept proportion: 0.9-0.91 g / cubic centimeter Molding shrinkage: 0-2.5% 1. Molding temperature 160-220 DEG C Drying condition The material properties of low density, strength and stiffness, hardness and heat resistance are better than that of low pressure polyethylene, can be used at 100 degrees. With good electrical insulation and high not affected by humidity, but the low temperature brittle, do not wear aging. Suitable for making general mechanical parts, corrosion resistant parts and insulation parts editor the performance of the section forming a crystalline material, moisture absorption is small, easy occurrence of melt fracture, long-term contact with the hot metal is easy to decompose. The good liquidity, but the range of shrinkage and shrinkage value, prone to shrinkage deformation. 3. Dent, cooling speed, pouring system and cooling system should slow cooling, and pay attention to the control the molding temperature. The temperature low direction is obvious. Especially when the low temperature and high pressure, mold temperature below 50 degrees, the plastic is not smooth, easy to produce adverse weld, leaving marks, 90 degrees or more prone to warping The plastic wall thickness should be uniform, to avoid the lack of glue, sharp corners, to prevent stress concentration. Under certain conditions can easily break down common products: pots, barrels, furniture, thin film, woven bag, bottle cap, bumper etc.. Polypropylene also includes copolymers of propylene with a small amount of