单分散球形纳米碳酸钙制备研究.PDF

282 非金属矿 Vol.28 o.2 2005 3 　　　　　　　　　　　　　　　　 on-Metallic Mines　　　　　　　　　　　　　　　　　 Mar., 2005 ＊ 1 1 1 2 陈先勇 　唐　琴 　史伯安 　周贵云 (1　, 　445000;2　, 　610065) 　　采用间歇鼓泡碳化法, 初步探讨了单分散球形纳 碳酸钙制备的可行性。考察了碳化反应温度、灰乳密度、添加剂等因素对碳 酸钙粒子粒径和形貌的影响。结果表明, 在碳化温度为20℃左右、灰乳密度为 1.07(d )的条件下, 加入少量复合添加剂PBTCA 和CTAB, 可制 得粒度分布均匀、分散性好、平均粒径为40nm 左右的球形碳酸钙粒子。 　球形纳 碳酸钙　制备　单分散　添加剂 Study on Synthesis of Monodispersed Spherical anometer Calcium Carbonate 1 1 1 2 Chen Xianyong 　Tang Qin 　Shi Boan 　Zhou Guiyun (1　Hubei Institute for ationalities, Enshi　445000;2　Institute of Chemical Engineering, Sichuan University, Chendu　610065) Abstract 　Monodispersed spherical nanometer calcium carbonate particles weresynthesized by the batch bubbling carbonation method.Theinflu- ence of temperature, specific density of Ca(OH), additives on Its sizeand morphology were discussed.It was shown that, the spherical nanometer calci- 2 um carbonate particles with mean size 40nm and more narrow size distribution and good dispersivity could be prepared under temperature about 20℃, specific density of Ca(OH)1.07(d )and compound additives of PBTCA and CTAB. 2 Key words　spherical nano-CaCO 　synthesis　monodispersion　additive 3 　　、, (), (, 1.5L, 、、、、[1～3] 。 2.5 ∶1, ),(, , , , ), 、、 (), pH-25 (), , 。 JSM-5900LV (JEOL ), X Pert Pro , 。 MPDX (Philips)。 ,, 1.2 　实验方法　35.0 ～60.0g , , ,, 0.5h , ,[4 ～6]。 、。 , , 、, , 、。, 25%～35%(V%), , , 600r/min 。pH 、、 , (pH=7.0), [7,8] , 、。 。 ,、、