低温烧结制备的ndfeb磁体结构和磁性能.pdfVIP

工艺·技术·应用 低温烧结制备的NdFeB 磁体结构和磁性能 赵 彪，何 静 （上海应用技术学院城市建设与安全工程学院，上海 201418 ） 摘 要：分别采用常规烧结和低温烧结制备了 NdFeB 磁体，对样品的结构和性能进行了对比分析。结果表 明，低温烧结磁体的晶粒均匀细致，晶界平滑、清晰，富钕相均匀弥散地分布于晶粒周围，微观组织得到改善； 剩磁基本没有改变，内禀矫顽力、取向度、最大磁能积均有所提高。 关键词：NdFeB 磁体；低温烧结；显微结构；磁性能；取向度 中图分类号：TM273 文献标识码：A 文章编号：1001-3830(2012)06-0046-03 Microstructure and magnetic properties of NdFeB magnet prepared by low-temperature sintering ZHAO Biao, HE Jing College of Urban Construction and Safety Engineering, Shanghai Institute of Technology, Shanghai 201418, China Abstract: NdFeB magnets were prepared by conventional sintering and low-temperature sintering, respectively, and their microstructure and magnetic properties were analyzed coparatively. The results showed that low-temperature sintered magnet exhibits uniform and fine grains, smooth and clear grain boundary, Nd-rich phase uniformly dispersed around the grains.As a result, magnet was obtained with almost the same remanence, and improved intrinsic coercivity, degree of orientation, and maximum energy product by low temperature sintering. Key words: NdFeB magnet; low-temperature sintering; microstructure; magnetic properties; degree of orientation 必然选择。目前，国内钕铁硼生产企业普遍采用添 1 引言 加中重稀土元素提高磁体性能，尤其是生产 SH、 作为第三代稀土永磁材料的钕铁硼磁体，自从 UH 和EH 以上高矫顽力产品时，往往更是过量添 1983 年由日本住友金属和美国 GM 公司首先商品 加。国外如日本Neomax 、信越和德国VAC 等钕铁 化以来[1]，由于具有高剩磁、高矫顽力和高磁能积 硼磁体制造先进企业，更为注重产品的微观组织结 的特点，广泛应用于电力电子、通讯、信息、电机、 构和杂质控制[2]，而非只通过中重稀土添加来提高 交通运输、办公自动化、医疗器械、军事等领域， 材料磁性能。 并使一些小型、高度集成的高新技术产品的应用成 高性能钕铁硼磁体的磁性能，如矫顽力Hc 和 为可能，如硬盘用音圈电机（VCM ）等。随着日 最大磁能积(BH)max 等是结构敏感