低温下镍的磁化强度与温度的关系 on the relationship between magnetization of nickel and temperature at low temperature.pdfVIP

研究·分析·实验 低温下镍的磁化强度与温度的关系 刘月新 （湖南理工学院物电系，湖南岳阳 414006 ） 摘 要：依据实验测定的低温下镍的磁化强度与温度的关系曲线，采用自旋波的量子化理论可推得低温下 磁振子的磁化强度的变化分数 ΔM / M (0) 与 T3/2 成正比。此结论与低温下镍的磁化强度与温度关系的实验曲线十 分接近。 关键词：镍；磁化强度；低温；自旋波；量子化 中图分类号：O482.54 文献标识码：A 文章编号：1001-3830(2006)03-0013-03 On the Relationship Between Magnetization of Nickel and Temperature at Low Temperature LIU Yue-xin Physics Department, Hunan Institute of Science and Technology, Yueyang 414006, China Abstract: According to the curve of the relationship between the magnetization of metal nickel and temperature measured by experiment, applying quantization theory of spin wave, the magnetization variation ratio ΔM / M (0) of the magnon with a T3/2 dependence at low temperature was derived, which is in accordance with experimental results. Key words: nickel; magnetization intensity; low temperature; spin wave; quantization 铁磁材料的磁化强度随温度的变化在居里温 m=tanh(m/t) （2 ） 度以下可以用平均场理论近似求得，但在低温下此 将（2 ）式左端和右端作为m 的函数分别作图，如 方法与实验偏差较大。本文则依据弗·洛波赫得到 图 1，两条曲线的交点给出了不同温度下的 m 值。 的低温下镍的磁化强度实验曲线，采用自旋波量子 临界温度为 t=1 ，即 T =N μ 2 λ /K ，这样可以得到 C B 化理论分析了低温下镍的磁化强度与温度的关系， M-T 曲线，如图2[2] 。 推得的理论结果与实验结果很接近。 由图2 可见，随温度上升，磁化强度平滑地减 1 居里温度附近磁化强度与温度的关系 小，至 T=TC 时降为零。 在居里温度以下接近该温度时，铁磁材料的磁 2 低温下镍的磁化强度实验曲线 化强度与温度的关系可以用平均场近似求出。对自 在低温情况下，当 T«TC 时，（2 ）式中双曲正 旋 S=1/2 ，此表达式为[1] 切函数宗量大，因此，tanhξ ≅ 1 − 2e−2ξ 。取低级近 M Nμ tanh(μλM / K B