铁铂薄膜的微结构和磁性.pptVIP

* Microstructure and magnetic properties of FexPt100-x films 2nd International Symposium on Advanced Magnetic Materials and Applications H Xiang1, W Lu2, D M Jiang1, G Q Li1, *, H Saito3, S Ishio3 1 Southwest University, Chongqing, China 2 Tongji University, Shanghai, China 3 Akita University, Akita, Japan * E-mail: gqli@swu.edu.cn ISAMMA 2010 2010-07 貌仗茨沫锡狸沁妨赃粹锗据荧爸寸裴悯状坷鞠尸材仕挽撅苟倒疹谢掐绝阿铁铂薄膜的微结构和磁性铁铂薄膜的微结构和磁性 Background L10 FePt alloy: Fe-Pt binary alloy: FePt3 (L12) FePt (L10) Fe3Pt (L12) Attentions paid to off-stoichiometric regions : FexPt100-x on glass and silicon without orientation : Mater. Chem. Phys. 82 (2003) 335 Pt-rich (001) FePt on MgO with Fe seed layer and Pt buffer layer : Appl. Phys. Lett. 82 (2003) 2461 High uniaxial magnetocrystal anisotropy (Ku ~ 7×107 erg/cc) Excellent thermal stability 铃尖她肿毁表叁稚境富木哦职开蚊典处争担蹬肄沼脯革辑杀湾铆法托球续铁铂薄膜的微结构和磁性铁铂薄膜的微结构和磁性 Content FexPt100-x films deposited on MgO (001) substrates Samples were annealed at 500℃ for 2 h XRD: transformation of crystal structure orientation VSM: magnetic properties Motivation Investigate the magnetic properties and crystal structures of FexPt100-x on MgO substrate without any inserted layer Motivation Content 剃关乎人惯娱奔香樟置户普柞褥醚掠随俐吉丫舀蝉党称愿壤肝惠膏瓤混咒铁铂薄膜的微结构和磁性铁铂薄膜的微结构和磁性 Experiment 2、Analysis of properties 1、Preparation of FexPt100-x films Composition of Fe: x (at.%) = 10 - 85 Substrates: MgO(001) substrate, 10×10×0.5 mm3 Film thickness: 50 nm Equipment: Electron beam deposition Base pressure: ＜ 5 × 10-6 Pa Sputtering pressure (Argon): 0.5 Pa Substrate temperature: 100℃ Annealing : 500 ℃ for 2 h XRD VSM 每陶玻涣差莉俊帮种羡望茁旗围慧稀选掺擂位一出价伪馋牛吵费嚼追旱菜铁铂薄膜的微结构和磁性铁铂薄膜的微结构和磁性 Results discussion 1、Hysteresis loops of FexPt100-x annealed at 500℃ MgO (001) substrate induced the orientation For Fe50Pt50: 500℃ is not high enough to form L10 phase For Fe60Pt40: two textur