试论大体积砼施工技术摘要：随着建行业的迅速发展，高层建筑物，高耸结构及大型设备基础大量的出现大体积砼已经被广泛应用，大体积砼与普通钢筋砼相比，具有结构厚，体形大，钢筋密，砼数量多，工程条件复杂等特点。大体积砼是指其最小断面的尺寸仍大于1000mm以上的砼结构,大体积砼施工技术与施工质量、工程造价、结构安全等密切相关。大体积砼施工的技术十分复杂,因此对于施工的技术有更高的要求,本文在此论述了大体积砼的施工技术,以及提高大体积砼质量的一些途径,避免裂缝的产生,确保施工质量。 关键词：大体积砼 , 混凝土,裂缝措施,施工质量 , 施工技术 Abstract: with the rapid development of the industry built, high-rise buildings, the towering structure and large equipment foundation appear a large number of mass concrete has been extensively applied, mass concrete and reinforced concrete ordinary compared, the structure is thick, the figure is big, reinforced close, concrete number, the engineering condition complex etc. Characteristics. Mass concrete is to show its minimum sections of more than 1000 mm size is still more concrete structure, mass concrete construction technology and construction quality, engineering cost, the safety of the structure, and so closely related. Mass concrete construction technology is very complex, and the construction technology for a higher request, in this article discusses the mass concrete construction technology, and improve the quality of the mass concrete ways to avoid the cracking of the, to ensure the construction quality. Keywords: mass concrete, concrete, the crack measures, construction quality, construction technology 中图分类号： [TQ178] 文献标识码：A 文章编号： 1产生裂缝的主要原因 1.1水泥水化热 水泥在水化过程中要释放出一定的热量，而大体积混凝土结构断面较厚，表面系数相对较小，所以水泥发生的热量聚集在结构内部不易散失。这样混凝土内部的水化热无法及时散发出去，以至于越积越高，使内外温差增大。单位时间混凝土释放的水泥水化热，与混凝土单位体积中水泥用量和水泥品种有关，并随混凝土的龄期而增长。由于混凝土结构表面可以自然散热，实际上内部的最高温度，多数发生在浇筑后的最初3～5天。 1.2外界气温变化 大体积混凝土在施工阶段，外界气温的变化对防止大体积砼裂缝产生起着很大的影响。砼内部的温度是由浇筑温度、水泥水化热的绝热温升和结构的散热温度等各种温度叠加之和组成。浇筑温度与外界气温有着直接关系，外界气温愈高，砼的浇注温度也就会愈高。 1.3砼的收缩 砼在空气中硬结时体积减小的现象称为砼收缩。砼在不受外力的情况下的这种自发变形，受到外部约束时，将在砼中产生拉应力，使得砼开裂。引起砼的裂缝主要有塑性收缩、干燥收缩和温度收缩等三种。在硬化初期主要是水泥石在水化凝固结硬过程中产生的体积变化，后期主要是砼内部自由水分蒸发而引起的干缩变形。 2大体积混凝土防裂的措施 分析大体积混凝土裂缝的成因和工程实践表明：控制水化热，改变约束条件，提高混凝土极限拉伸能力等措施都有效的防止裂缝的形成。 2.1原材料选择及配合比设计 水泥。不同品种水泥水化所释放的热量各异，大体积混凝土宜选用水化热低，凝结时间长的水泥，在