直接法制备锰锌铁氧体粉料的原理、工艺与性能 principle, process and properties of mn-zn soft magnetic ferrite powders by direct-method.pdfVIP

直接法制备锰锌铁氧体粉料的原理、工艺与性能 彭长宏，白本帅，唐谟堂 (中南大学冶金科学与工程学院，湖南长沙410083) 摘要：介绍了直接法制备锰锌软磁铁氧体材料的工艺流程、特点及原理。以铁屑、软锰矿和锌烟灰为原 料，进行了500t／a规模的直接法制取低功耗软磁共沉粉的工业试验。结果表明，共沉粉杂质元素含量低，配比 准确；以此共沉粉为原料，进行了单槽和多槽混合共沉粉铁氧体工艺实验，所得锰锌软磁铁氧体样环的磁性能 完全迭到日本TDK公司的PC30标准，且所有指标均超过国内某公司同类产品。 关键词：直接法；锰锌铁氧体粉料；工艺；磁l生能 中图分类号：TM277+．1：TFS03．2文献标识码：，A and ofMn-ZnSoft Principle，ProcessProperties Magnetic FerritePowdersDirect-method by PENG Ben—shuai，TANGMo—tang Chang—hong，BAI Scienceand South 410083，China University,Changsha CollegeofMetallurgicalEngineering,Central this and of ofMn一盈soft Abstract：In principlepreparation paper,thetechnologicalprocess．characters ferritedirectmethodwere scrap andcoarseoxide-zincmaterials，the magneticby introduced,Usingiron，pyrolusite industrialscale withannual of500t were experiment capacity co-precipitationpowdersperformed．neexperimental that madedirect-methodhavethe oflowcontentof resultsdemonstrated advantage co-precipirationpowdersby made andmulti—Vessel andaccurate onferrite from technological single—vessel impurities PreSCriPtion．Theexperiments bv werealsoearriodout．r111e dataconfirmthat ofthe direct-method performance co-precipitation，powders experimental