利用配位原理在氧化铝模板中沉积氧化锌纳米线 张灵翠，阮永丰*，王丹丽，邱春霞 （天津大学理学院 邮编 300072） 摘 要 本文报告了一种新的合成氧化锌纳米线的方法。采用具有挥发性的氨水为配位剂，与可溶性的锌盐反应配制锌氨配合物溶液—前驱液，以氧化铝模板的孔道为微反应器，运用配位平衡及配合物稳定性原理，通过改变实验参数条件，在氧化铝模板中沉积氧化锌纳米线。文中对氧化锌纳米线的形成过程以及生长机理进行了分析，并结合现代测试手段对AAO/ZnO组装体的形貌、组成进行了表征。实验结果表明，所合成的纳米线均具有氧化铝模板孔道的形态特征，且孔的填充率非常高。 关键词 阳极氧化铝；氧化锌纳米线；配位法 The Fabrication of ZnO Nanowire Arrays in Porous Anodic Alumina Template by Coordination Reaction Zhang Lingcui, Ruan Yongfeng, Wang Danli, Qiu Chunxia (School of Science, Tianjin University, Tianjin 300072, China) Abstract: A new feasible method named “coordination method” has been developed to fabricate ZnO nanowire arrays. Taking zinc amino-complex as precursor, we have synthesized ZnO nanowires in the holes of alumina template. Some modern analysis and testing technologies were adopt to characterize the morphology and composition. The results showed that all the arrays had the same structures as AAO. And the injection ratio of ZnO in AAO was extremely high. Key words: Anodic Aluminum Oxide (AAO); Znic Oxide(ZnO) Nanowire Arrays; Coordination Method 1 引言 ZnO因具有较高的化学稳定性、较大的禁带宽度（Eg＝3.4eV）和较高的激子束缚能（60meV），并具有独特的电学、发光和光化学性质[1]，在太阳能电池、催化、气敏、纳米激光、光电子器件[2]以及下一代半导体材料等领域，均有广阔的应用前景，因而受到了极大的关注。目前运用氧化铝模板制备氧化锌纳米线的方法有“溶胶凝胶法”[3]、“电泳沉积法”[4]、“电沉积法”[5]、“直接沉淀法”[6]等多种方法，上述这些制备方法各存在自己的优缺点，不利于工业化的生产，从而限制了纳米材料的发展。本文利用配位法制备氧化锌纳米线的过程工艺简单，条件易于控制，实验现象具有很高的重复性，为今后的工业化生产打下了坚实的基础。 ( 2 实验过程 2.1 试剂、仪器和测试 实验仪器：WYJ型直流稳压电源，真空管式高温烧结炉，电热恒温水浴锅，KQ -100DB型数控超声波清洗器，FA1204型电子天平，磁力搅拌器，送风型定温干燥箱。实验试剂：所用到的试剂均为分析纯。实验测试：采用美国FEI公司制造的Nanosem 430型热场发射扫描电子显微镜、日本电子公司制造的JEOL 100CX-Ⅱ型场发射透射电子显微镜以及日本理学制造的D/Max-2500 X射线衍射仪进行分析。 2.2 实验原理 运用配位原理在氧化铝模板中制备氧化锌纳米线阵列，整个制备过程中所涉及到的主要化学反应简单表示如下： NH3 + H2 O NH4＋+ OH - （1） Zn2+ +2OH - Zn(OH)2 ↓ （2） Zn(OH)2＋nNH3·H2OZn（NH3）n2+ （3） Zn2+＋n NH3 Zn（NH3）n2+ （4） Zn(OH)2·nH2OZnO+(n+1)H2O （5） 其中式3是配位法制备氧化锌纳米线的核心，包括了两次转化过程，即氢氧化锌向锌氨配合物转化的过程和锌氨配合物向氢氧化锌沉淀转化的过程。 21）向多孔氧化铝模板的纳米级孔道输送的物质是前驱液——锌氨配合物溶液，该前驱液的粘度与水的粘度