试论钢筋混凝土构件裂缝原因及其防治对策.docVIP

试论钢筋混凝土构件裂缝原因及其防治对策中图分类号：TU37 文献标识码： A 文章编号： 摘要:钢筋混凝土是应用最为广泛的建筑材料，主要构件包括了梁、板、柱、墙等。在钢筋混凝土的建设和使用过程中，构件出现裂缝而影响工程质量屡见不鲜。为此，本文分析了荷载、温度变化、基础位移、钢筋锈蚀等作用下钢筋混凝土构件裂缝的形成原因，总结了不同裂缝的防治对策，旨在减少构件裂缝的出现，保证钢筋混凝土的质量。 关键词:钢筋混凝土构件；荷载裂缝；温度裂缝；原因；防治对策 Abstract: the reinforced concrete is most widely used building materials, main components including the beam, plate, column, wall and so on. In a concrete construction and the use of process, component and influence the project quality cracks in common. Therefore, this paper analyzes the load, temperature change, foundation displacement, and rust corrosion function of reinforced concrete structures such as the reasons for the formation of crack, and summarizes the different fracture prevention measures aimed at reducing component occurrence of crack and guarantee the quality of the reinforced concrete. Keywords: reinforced concrete structures; and Load crack; Temperature crack; Reason; Countermeasures to prevent and control 众所周知，钢筋混凝土是建筑施工中常见的材料，是一种由砂石集料、水泥、水及其他外加材料混合而成形成的非匀质脆性材料。钢筋混凝土已经普遍用于工业和民用建筑中。但多年来，钢筋混凝土构件的裂缝一直是施工中最为常见和难以克服的弊病，一些有害裂缝会使混凝土内部钢筋产生腐蚀，降低了钢筋混凝土材料的承载能力、耐久能力及抗渗能力，不仅影响建筑物的使用寿命，甚至威胁建筑物的安全性能。因此，研究钢筋混凝土构件的裂缝产生原因及防治具有重要意义。 1 钢筋混凝土构件裂缝原因 钢筋混凝土构件的裂缝是施工中常见和难以克服的弊病。在各种作用下，都会产生变形，这种现象称为作用效应。随着某种作用的增强，作用效应也在不断的积累，同时构件内部的能量(应变能)也在不断积累，当变形值达到其自身对变形的承受极限时，钢筋混凝土构件就会出现裂缝，将内部积累的能量释放掉，从而使构件在新的状态下达到平衡。如果这种作用继续增强，则会在混凝土内部重新积聚能量。随着能量的不断积累与释放，混凝土内部的裂缝也会不断地产生和扩展，从而最终导致该构件的破坏。现浇钢筋混凝土构件上的作用主要包括荷载作用、温度作用、干缩作用、基础位移等。这些作用对构件的影响特点不一样，所以裂缝的形式及特点也就各有不同。 1.1 荷载作用对构件裂缝的影响分析 钢筋混凝土构件主要有梁、板、柱、墙等，在正常使用条件下，钢筋混凝土梁、板主要承受弯矩作用，柱和墙主要承受压力作用，由于各种构件的受力形式不同，所以裂缝出现的特点及危害程度也大不相同。 1.2 温度变化对构件裂缝的影响分析 水泥中的铝酸三钙(3CaO·Al2O3)和硅酸三钙(3CaO·SiO3)在水化过程中会产生大量的水化热，并且该水化热大部分集中在浇筑后的3d～7d内产生，通常7d内产生的热量可达总热量的80%左右。水化热的产生，提高了混凝土的温度，从而又加速了水泥水化的速度，致短期内产生更多的水化热。 1.3 混凝土收缩对构件裂缝的影响分析 混凝土终凝前，水泥水化反应，分子链逐渐形成，出现泌水和水分大量蒸发，混凝土失水收缩，同时骨料因自重下沉，在骨料下沉过程中若受到约束(如模板、钢筋、管线等)，便形成塑性收缩裂缝。混凝土终凝后，随着水分蒸发，湿度逐步降低，混凝土体积产生缩水收缩(干缩)。 1.4 钢筋锈蚀对构件裂缝的影响分析 如果混凝土质量较差或保护层厚度不足，表层混凝土受二