7面上形变诱导铁素体相变形核机理研究.docVIP

ZrC/奥氏体相界面上形变诱导铁素体相变形核机理研究 唐明华1,2　　刘志义1　　汪新衡2　　胡双开3 （1.中南大学材料科学与工程学院，湖南长沙　410083；　2.湖南工学院机械系，湖南衡阳　421002； 3.湖南衡阳钢管(集团)有限公司，湖南衡阳　421001；) 摘　要　采用Gleeble-1500热模拟试验机进行单向压缩热模拟试验，研究了含ZrC粒子的K—S关系，同时在DIFT相变中发生了排碳过程。作者认为ZrC/奥氏体相界面上形变诱导铁素体相变是受长程扩散控制的扩散型相变。 关键词　ZrC粒子；低碳锰(铌)钢；形变诱导铁素体 Study of Nucleating Mechanism of Deformation Induced Ferrite Transformation at ZrC/Austenitic Interface TANG Ming-hua1,2　　LIU Zhi-yi1　　WANG Xin-heng2　　HU Shuang-kai3 School of Materials Science and Engineering Central SouthUniversity,ChangshaHunan,410083,china. 2.Department of Mechanical Engineering of Hunan InstituteTechnology,HengyangHunan,421002,China. 3.Hunan Hengyang Steel Tube (Group) CO,LTD,HengyangHunan 421001,china.) ABSTRACT　　The nucleating mechanism of ultra-fine ferrite of deformation induced ferrite transformation of low carbon manganese (niobium) steel obtaining ZrC particles during undercooled austenite deformation was investigated by unidirectional compression thermal simulating experiment with Gleeble-1500.The results show that ZrC particles can hinder dislocation-motion and form concentrate degree of the located deformation in austenite when ZrC particles which definite radius and suitable volume fraction is dispersed distributed in basal phase,thus improve ferrite nucleating rate and accelerate DIFT process which leads to the further refinement microstructure.The ferrite nucleating at ZrC/austenite interface have unsaturated and heterogeneity behaviour of nucleating location,regenerate α phase has ultra-fine grains character.and K—S relation is existed between ferrite and parent phase austenite ,simultaneously,diffusion of carbon atoms happened during DIFT.The author regard that the deformation induced ferrite transformation at ZrC/austenite interface is subject to diffused-pattern phase change which controlled by long-path diffusion. KEY WORDS　　ZrC particles;low-carbon manganese (niobium) steel ;deformation induced ferrite transformation;ultra-fine grain;phase change mechanism 伴