浅议水运工程施工混凝土质量中常见问题及防治措施.docVIP

浅议水运工程施工混凝土质量中常见问题及防治措施摘要: 水运工程施工过程中的混凝土质量问题已成为对水运工程质量产生危害和影响工程质量进一步提高的重要原因，本文拟从原材料控制、配合比控制、拌和过程控制、浇筑过程质全控制、养护、泥凝土的质量检查等方面对水运工程施工中混凝土质量的影响因素进行了深入的探讨,并从混凝土原材料、拌和物、施工工艺及养护等方面,提出了一系列防控措施。 关键词：水运工程施工；混凝土；问题因素；防治措施 Abstract: water project construction process of concrete quality problem has become a water project quality to produce harm and influence the project quality to further improve the important reason, this article, from the control of raw materials, mixing ratio control, mixing process control, quality control, all the construction process of maintenance, mud of soil quality inspection of water transportation engineering construction, the influence factors of concrete quality thoroughly discussed, and from raw materials, mixing concrete thing, construction technology and the maintenance, puts forward a series of prevention and control measures. Keywords: port waterway engineering construction; Concrete; Problem factor; Prevention and control measures 中图分类号：TU528文献标识码：A 文章编号： 随着国家对基础设施建设投资的加大,水运建设进入了前所未有的高潮。如何加强水运工程施工中混凝土的质量管理,确保工程质量,是当前水运工程施工中被广为关注的焦点。拟从原材料控制、配合比控制、拌和过程控制、浇筑过程质全控制、养护、泥凝土的质量检查等方面对水运工程施工中混凝土质量的影响因素进行了深入的探讨,并从混凝土原材料、拌和物、施工工艺及养护等方面,提出了一系列防控措施。 1混凝土工程质量影响因素及质量控制 1.1原材料 1. 1. 1原材料对混凝土质量的影响 配制混凝土所用原材料直接影响混凝土结构的强度、刚度及安全性能,建筑用原材料的质量不合格,将导致结构承载能力下降,造成结构裂缝,酿成房屋渗漏,甚至倒塌。经过几年的总结与分析,发现原材料引起混凝土质量差的主要因素有: 1)水泥品种、标号直接影响混凝土的质量、性能和适用范围。因为水泥颗粒越细,对水化发展也越块、越充分,则混凝土硬化快、强度、滗水性及和易性好。水泥凝结过早,施工操作难以掌握;凝结过迟,浇筑的混凝土不能及时硬化,会妨碍正常施工,影响工程质量和进度;水泥标号不宜过高或过低,水泥标号过低,将增大水泥用量,经济上不合理;水泥标号过高,则混凝土按强度要求的水灰比将相应偏大,这样不仅会增加水泥用量,而且还会降低混凝土的密实性,使耐久性受到影响。如按混凝土耐久性确定其水灰比,则混凝土强度又将超出设计要求,使高标号水泥遭到更大浪费。水泥受潮、过期、结块严重影响混凝土的质量。 2)砂的细度模量、空隙率、有害杂质对混凝土强度、耐久性产生重要影响。因为砂越细,总表面积越大,需包裹砂粒表面和润滑砂粒用的水泥浆量越多;空隙越大,所需填充空隙的水泥浆量也越多,这不仅需要多用水泥,而且还影响混凝土的强度和耐久性;砂中有害杂质对水泥有侵蚀作用,粘土、粉土会降低混凝土的强度、抗渗性及抗冻性,当砂中含有活性氧化硅时,能与水泥中的碱分起作用,发生骨架膨胀反应,使混凝土产生裂缝。 3)石子的级配和最大粒径对混凝土质量影响较大。级配越好,其空隙率及总表面积越小,不仅能节约水泥用量,而且混凝土的和易性、密实性和强度也越高;石子粒径太大,增大水泥用量,导致混凝土 收缩量加大,产生收缩裂缝。 4)拌合用水的质量和种类也将影响混凝的质量,因为它和水泥能发生一系列的化学反应,生成硬