浅议灌浆在水工建筑物中作用摘要:伴随着现代社会的高速发展,工程建设的实践和新技术的开发,灌浆材料、施工工艺、施工设备和效果检测等方面,都取得了重大的进展,在水利水电建设中得到了广泛应用,其中灌浆是把浆液灌入土壤或岩石地基中的空隙、裂隙、缝隙或洞穴用以减少渗透性,增加强度或减少地基变形等。灌浆材料根据所制成的浆液状态,可以分为:固粒状浆材和化学浆材。 关键词:灌浆；水工建筑 Abstract: with the rapid development of modern society, the construction of engineering practice and the development of new technology, grouting material, construction technology, construction equipment and testing effect, has made a great progress in the construction of water conservancy and electricity to a wide range of applications, including the slurry grouting is into the soil or rock foundation, crack, crack the gaps in the caves and were used to reduce permeability, increase the intensity or reduce the deformation of foundation, etc. Grouting material made from the state according to size, can be divided into: solid granular paste material and chemical pulp material. Keywords: grouting; Hydraulic structure 中图分类号：G267文献标识码：A 文章编号： 1 灌浆材料 首先说的是固粒状灌浆材料特性:(1)颗粒细。要具有一定的细度,以便进入裂隙,其粒径小于裂隙宽度的1/3才宜奏效。(2)浆液稳定性好。固体颗粒材料与水混合后,其颗粒在一定时间内应保持呈均匀分散的悬浮状态,并具有较好的稳定性和流动性。(3)胶结强度高。灌入裂隙中经过一定时间应能胶结成为坚硬的结石,起到充填与固结的作用。(4)结石强度高。结石要具有一定的强度、粘结力和抵抗侵蚀的能力,以保证灌浆效果的耐久性。水泥灌浆是使用最早也是使用最广的一种固粒状灌浆材料, 水灰比一般多为10∶1～0.6∶1,一般普通水泥的最大粒径在44μm～100μm范围内,由于颗粒粒径的限制,水泥浆液难于灌入渗透系数小于0.5cm/s的粗砂或裂隙宽度小于0.6mm的岩体中。通过水泥细度和掺合料的改进可解决以上问题。其中新型常用水泥主要包括以下几种。 (1)超细水泥:将水泥磨细至平均粒径为4μm,最大粒径为10μm,比表面积在8000m2/kg以上,这时浆体稳定性好,固结时析水少,有利于防止新的渗水通道产生,可灌入渗透系数在10-3cm/s～10-4cm/s的细砂中。超细水泥可以单独使用加固建筑物的地基,也可以混以水玻璃使用用于堵漏灌浆。 (2)硅粉水泥:硅粉是生产硅或硅铁合金的副产品,直径约为0.1μm的细微玻璃状球体。它是一种高活性材料,极细的硅粉颗粒可使浆液稳定,水泥颗粒不沉降,浆液亦不泌水,可得到触变性能的浆液。掺入硅粉后水泥浆体具有如下影响:增加水泥浆液初始粘度,需要掺加外加剂降低粘度;有好的触变性;浆液稳定性提高;固结体抗压强度显著提高;孔隙分布更细,抗渗、耐久性能优良。 2 化学灌浆材料 水泥浆液由于颗粒粒径的限制,难于灌入一些细微裂缝。水泥灌浆还受水流流速的限制,一般灌浆规范中规定,地下水流速不大于600m/d。但在实际应用中地下水流速小于80m/d才可灌注水泥浆,超过需在水泥浆液中掺加速凝剂。遇到基础涌水、基岩夹泥断层破碎带,水泥灌浆便无法操作。 化学灌浆材料比水泥具有好的可灌性,而且能按工程的需要调节浆液的胶凝时间,故也适用于有流动水部位的堵漏或防渗。有的化学灌浆材料还具有较高的粘结强度和抗拉、抗压强度,适用于混凝土结构补强处理。化学灌浆在改进工程质量、提高施工进度和经济合理性方面都有作用。化学灌浆材料具有如下特性:其一是浆液粘度低,可灌性好,能在较低压力下灌入细微裂缝。其二是凝胶体具有较好的密实性、防渗性和耐久性,用于补