三聚氰胺甲醛树脂的醚化工艺研究..doc

三聚氰胺甲醛树脂的醚化工艺研究 摘要 本文通过分别在不同的pH值、羟甲基化阶段不同的脱水量、反应时间与反应温度等条件下合成作为交联剂的三聚氰胺树脂，同时对羟甲基三聚氰胺树脂与甲醇、乙醇、异丙醇、正丁醇四种不同的醚化剂进行醚化，并对产物的性质和结构做了测定和表征。研究结果表明：醚化反应在pH 3~4范围内，羟甲基化阶段的脱水量在40%左右，以甲醇为较好的醚化剂。 关键词：三聚氰胺树脂 交联剂 醚化 一元醇 The ethered technology of Melamine formaldehyde resin Abstract The paper designs methylol melamine and methanol, ethanol, isopropanol, butanol four different ether agent , respectively, in different pH, hydroxymethyl of the different stages of dehydration , reaction time and temperature conditions, synthesizes melamine resin as a cross-linker of melamine, and the nature and structure of the final product is determined and charactered . The results show that: ether reaction in the pH 3 ~ 4,within hydroxymethyl stage of dehydration in about 40 percent of methanol ether is more ideal. Key words：Melamine resin Crosslinker Etherification Alcohol 目录 前言………………………………………………………………………………1 1.1 氨基树脂的概述…………………………………………………………1 1.2 醚化三聚氰胺树脂的发展………………………………………………1 1.3 醚化三聚氰胺树脂的应用………………………………………………1 1.3.1 醚化三聚氰胺树脂在丙烯酸涂料中的应用……………………2 1.3.2 醚化三聚氰胺树脂在醇酸树脂漆中的应用…………………2 1.3.3 醚化三聚氰胺树脂在聚氨酯涂料中的应用…………………2 1.4 研究内容…………………………………………………………………2 实验部分………………………………………………………………………2 2.1 实验材料及实验仪器……………………………………………………2 2.2 生产工艺及原理…………………………………………………………3 2.2.1 工艺路线………………………………………………………3 2.2.2 化学反应原理…………………………………………………3 2.3实验步骤…………………………………………………………………4 2.3.1 羟甲基化反应…………………………………………………4 2.3.2 脱水…………………………………………………………4 2.3.3 醚化反应………………………………………………………4 2.4 醚化三聚氰胺树脂的红外和热失重分析图…………………………4 结果与讨论……………………………………………………………………4 3.1 不同pH值对醚化反应的影响…………………………………………4 3.2 羟甲基化阶段的脱水量对三聚氰胺树脂醚化反应的影响……………5 3.3 选用不同的醚化剂对醚化反应的影响…………………………………8 3.4 反应时间与固化反应的关系…………………………………………13 4. 结论……………………………………………………………………………14 参考文献…………………………………………………………………………15 致谢………………………………………………………………………………15