水工建筑物中混凝土施工裂缝控制措施.docVIP

水工建筑物中混凝土施工裂缝控制措施摘要：裂缝的存在和发展，破坏了水工建筑物结构的整体性，影响了水工建筑物的结构受力状况与稳定。给水工建筑物结构的运行事带来不确定性，而且易导致水工建筑物内部与钢筋锈蚀，降低水工建筑物结构的耐久性，甚至会引起渗透变形，危及水工建筑物的结构的稳定性。本文主要分析混泥土施工裂缝的成因，探讨防治措施，对水利工程建筑物的应用有着极其重要的意义。 关键词: 水工建筑物；混凝土；裂缝；控制措施 Abstract: the existence and development of cracks, destroy the hydraulic structures the integrity of the structure, the influence of the hydraulic structures structure stress and stability. The hydraulic structures of the structure to run things the uncertainty, and easy to hydraulic structures and internal corrosion of reinforcement, reduce hydraulic structures of the durability of the structure, can cause even seepage deformation, endanger the stability of the structure of hydraulic structures. This paper analyzes the causes of cracks mixes clay construction, this paper discusses the prevention measures, and the application of hydraulic engineering building is very important. Keywords: hydraulic buildings; Concrete; Crack; Control measures 中图分类号：TU37文献标识码：A 文章编号： 裂缝是混凝土结构中普遍存在的一种现象，在水利水电工程施工中,混凝土是工程中使用最普遍，用量广泛的一种混合材料。虽然使用率高，但混凝土均匀性差，离散性大，特别容易产生裂缝。它不仅会降低建筑物的抗渗能力，影响建筑物的使用功能，而且会引起钢筋的锈蚀、混凝土的碳化，降低材料的耐久性，影响建筑物的承载能力。因此，要对混凝土裂缝进行认真研究、区别对待，采用合理的方法进行处理，并在施工中采取各种有效的预防措施来预防裂缝的出现和发展，保证建筑物和构件的安全和稳定。 1工程概况 某水闸工程，右岸挡墙及右岸边墩在混凝土拆模后,发现了裂缝。裂缝特征如下:裂缝在水平方向上均发生在挡墙分仓的中部;裂缝在竖向并未完全贯通,大部分裂缝产生在挡墙3/4高度以下,挡墙顶部没有裂缝;裂缝缝宽在0.3mm左右,呈现中间宽,两头缩小的现象;有部分挡墙裂缝在两侧同处产生;部分裂缝从基础往上开裂,有些裂缝未从基础往上开裂。裂缝产生时间:出现裂缝的时间基本都在模板拆除后1～2d,有些裂缝在混凝土拆模后当天即发现。 2裂缝原因分析 2.1混凝土配合比 该工程出现裂缝的混凝土部位涉及挡墙和边墩,均使用了某牌P.O42.5水泥品种,这两种水泥产品质量较好,强度富余系数较高,因此造成混凝土实际强度值高出设计强度值较多,通过查阅相关的混凝土强度试验报告也证实了这一点,混凝土实测强度值大部分大于设计值200%以上,混凝土强度值的增加,加大了混凝土的水化热,提高了混凝土内部温度。在冬季施工混凝土的高水化热,一方面有利于混凝土温度的保持,避免混凝土受冻,保证混凝土强度;另一方面也带来了不利的因素。因此,水泥用量及水泥标号的选择是引起此工程混凝土裂缝的一个不可忽视的因素。另外,该工程使用的粗骨料最大粒径为25mm,对于尺寸较大的混凝土结构,控制胶骨比在1∶3以上,在质量相同时,其总面积减小,可减少水泥用量,减少水化热,在一定程度上有利于防止裂缝的产生。 2.2结构尺寸 本水闸工程中,挡墙的结构尺寸较大,大量的水化热聚积在混凝土内部而不易散发,导致内部温度急剧上升,而混凝土表面散热较快,这样就形成内外的较大温差,较大的温差造成内部与外部热胀冷缩的程度不同,使混凝土表面产生一定的拉应力。当拉应力超过混凝土的抗拉强度极限时,混凝土表面就会产生裂缝,这种裂缝多发生在混凝土施工中后期。结构尺寸