research on fire resistance of ultra-high-performance concrete研究超高性能混凝土的耐火性.pdf

Hindawi Publishing Corporation Advances in Materials Science and Engineering Volume 2012, Article ID 530948, 7 pages doi:10.1155/2012/530948 Research Article Research on Fire Resistance of Ultra-High-Performance Concrete Hao-wen Ye,1 Nai-qian Feng,2 Yan Ling-hu,1 Zhi-wei Ran,1 Li-xun Lin,1 Shi-kun Qi,1 and Yi Dong1 1 Technology Department, China Construction Fourth Engineering Division Corporation Ltd., Guangzhou 510665, China 2 Senior Scientists Association, Tsinghua University, Beijing 100084, China Correspondence should be addressed to Yan Ling-hu, linghuyan9@ Received 13 December 2011; Accepted 11 February 2012 Academic Editor: Gai-Fei Peng Copyright © 2012 Hao-wen Ye et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. Fire resistance of ultrahigh-performance concrete was measured under different temperatures and loadings. C120 concrete was prepared with 1 kg/m3 organic fiber and C120 concrete with 2 kg/m3 organic fiber and tested under loading at 30% ultimate ◦ ◦ ◦ strength when exposed to high temperatures of 200 C, 300 C, and 400 C, respectively. 1. Introduction (7) Water reducer, BASF polycarboxylic acid, solid con- tent: 40%; self-made naphthalene-sulfamate water At present, the research on the fire resistance of ultra-high- reducer. performance concrete equal to or greater than C100 has yet prevailed. However, concrete buildings usually get badly (8) P