新型纳米抗菌无机填料合成和其抗菌性能初步探究.docVIP

新型纳米抗菌无机填料合成和其抗菌性能初步探究[摘要] 目的 合成新型的纳米抗菌无机填料，为赋予牙科复合树脂抗菌性能提供新的思路。方法 通过有机合成的方法，首先合成了季铵盐：N,N,N-三甲基-3-（三甲氧基硅基）丙基-1-碘化铵，然后再将其枝接到纳米二氧化硅颗粒表面，得到新型纳米抗菌无机填料季铵盐修饰纳米二氧化硅，并对合成产物结构进行表征。然后以变异链球菌为对象，研究季铵盐修饰纳米二氧化硅的抗菌性能。结果 红外光谱分析表明，季铵盐成功地枝接到了纳米二氧化硅颗粒表面。与对照组相比，新型纳米抗菌无机填料对变异链球菌具有较强的杀菌作用（P0.01）。结论 季 铵盐修饰纳米二氧化硅颗粒具有较好的抗菌性能，可以用来提高牙用复合树脂的抗菌性。 [关键词] 复合树脂； 抗菌性； 无机填料； 季铵盐 [中图分类号] R 783.1 [文献标志码] A [doi] 10.3969/j.issn.1000-1182.2012.05.018 Study on synthesis on a novel nano-antibacterial inorganic filler and its antibacterial property Wu Junling1, Jin Chanyuan1, Nie Xiaomeng1, Zhou Kaiyun2, Zhou Chuanjian2. （1. Dept. of Prosthodontics, College of Stomatology, Shan-dong University; Shandong Provincial Key Laboratory of Oral Biomedicine, Jinan 250012, China; 2. Research Institute of Polymer Materials, School of Materials Science and Engineering, Shandong University, Jinan 250061, China） [Abstract] Objective To synthesize a novel nano-antibacterial inorganic filler and provide a new way to give dental composite resin antibacterial property. Methods Quaternary ammonium iodide N,N,N-trimethyl-3-（trimethoxysilyl） propan-1-aminium iodide were organically synthesized firstly and then the N,N,N-trimethyl-3-（trimethoxysilyl） propan-1-aminium iodide was grafted to the nano-silica particle to synthesize the antibacterial inorganic fillers nano-silica particle grafted with quaternary ammonium salt. All the products were analyzed and identified by infrared spectrum analysis. Then Streptococcus mutans were chosen as experimental object to analysis the antibacterial property of nano-antibacterial inorganic filler. Results Quaternary ammonium salt was grafted to the surface of nano-silica particles successfully by infrared spectrum analysis. Compared with the control group, the nano-silica particle grafted with qua-ternary ammonium salt had a strong bactericidal effect on Streptococcus mutans（P0.01）. Conclusion The nano-silica particle grafted with quaternary ammonium salt has a strong antibacteria