synthesis and photocatalytic properties of one-dimensional composite - nanowires合成及光催化性能的一维复合纳米线.pdfVIP

Hindawi Publishing Corporation International Journal of Photoenergy Volume 2012, Article ID 461291, 5 pages doi:10.1155/2012/461291 Research Article Synthesis and Photocatalytic Properties of One-Dimensional Composite Bi O -Bi CrO Nanowires 2 3 2 6 Qianqian Zhang,1 Baibiao Huang,2 Peng Wang,2 Xiaoyang Zhang,2 Xiaoyan Qin,2 and zeyan wang2 1 School of Chemistry and Chemical Engineering, Shandong University, Jinan 250100, China 2 State Key Laboratory of Crystal Materials, Shandong University, Jinan 250100, China Correspondence should be addressed to Baibiao Huang, bbhuang@ Received 11 July 2012; Accepted 29 July 2012 Academic Editor: Jiaguo Yu Copyright © 2012 Qianqian Zhang et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. One-dimensional composite Bi O -Bi CrO nanowires were successfully fabricated by a simple microwave-assistant hydrothermal 2 3 2 6 method. The successful fabrication of one-dimensional Bi O -Bi CrO nanowires can only be realized at pH value range 2 3 2 6 of 1–5 of the starting solution. The fabricated nanowires were characterized by X-ray powder diffraction (XRD), scanning electron microscope (SEM), transmission electron microscopy (TEM), UV-visible diffuse reflectance spectra (UV-Vis DRS), and photoluminescence (PL), respectively. The diameter of the nanowires varies from 30 to 100 nm; the length is a few microm