the corrosion behavior of ni3alni3v two-phase intermetallic compounds in various acidic solutionsni3alni3v两阶段金属间化合物化合物的腐蚀行为在不同酸性的解决方案.pdfVIP

Hindawi Publishing Corporation International Journal of Corrosion Volume 2012, Article ID 626240, 6 pages doi:10.1155/2012/626240 Research Article The Corrosion Behavior of Ni Al/Ni V Two-Phase 3 3 Intermetallic Compounds in Various Acidic Solutions Gadang Priyotomo, Hideyuki Momono, Sanat Wagle, Kenji Okitsu, Akihiro Iwase, Yasuyuki Kaneno, Rokuro Nishimura, and Takayuki Takasugi Department of Materials Science, Graduate School of Engineering, Osaka Prefecture University, 1-1 Gakuen-cho, Sakai, Osaka 599-8531, Japan Correspondence should be addressed to Gadang Priyotomo, gadangp@ Received 28 February 2012; Revised 21 March 2012; Accepted 5 April 2012 Academic Editor: Toshiaki Ohtsuka Copyright © 2012 Gadang Priyotomo et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. The corrosion behavior of the Ni Al/Ni V two-phase intermetallic compounds with and without minor elements (Nb, Co, and 3 3 Cr) to be composed of L1 phase (Ni Al) and a mixed phase of L1 (Ni Al) and D0 (Ni V) has been investigated by using an 2 3 2 3 22 3 immersion test in 0.5 kmol/m3 HCl, H SO , and HNO solutions. The surface morphology was observed before and after the 2 4 3 immersion test by scanning electron microscope (SEM). The results were compared to those of the L1 single-phase Ni (Si,Ti)