GUIDANCE NOTE 6 POST WELD HEAT （指导注意到6后焊接热量）.pdfVIP

Research, Education, Technical Support Information ABN 69 003 696 526 Unit 3, Suite 2, 9 Parramatta Road, Lidcombe, 2141. PO Box 6165, Silverwater, NSW 1811 Australia Phone: (02) 9748 4443 Fax: (02) 9748 2858 E-mail info@.au URL .au GUIDANCE NOTE 6 POST WELD HEAT TREATMENT OF WELDED STRUCTURES INTRODUCTION SCOPE During the fabrication process, welding is Post weld heat treatment in the context the most commonly used method of joining described here refers to the process of items together. The welding process reheating a weld to below the lower generally involves melting and subsequent transformation temperature at a controlled cooling, and the result of this thermal cycle rate, holding for a specific time and cooling is distortion if the welded item is free to at a controlled rate. No consideration has move, or residual stress if the item is been given to normalising of welds in securely held. There comes a point when the carbon-manganese and low alloy steels, to amount of residual stress can create potential solution annealing of stainless steels or to problems, either immediately or during the any precipitation hardening treatments to life of the welded structure, and it needs to other alloy materials. Therefore, almost by be