Welding parameters for duplex stainless steels （双相不锈钢的焊接参数）.pdf

Shop sheet 105 Welding parameters for duplex stainless steels © Sandvik Virtually all welding processes used on filler metal than in the base metal. It is heated to about 100°C (210°F) uniformly austenitic stainless steels are applicable generally accepted that the more highly and only after the weld preparation has to duplex stainless steels. This includes alloyed duplex stainless steel weld fillers been cleaned. Gas Tungsten Arc Welding (GTAW, TIG), are suitable for welding the lower alloyed Gas Metal Arc Welding (GMAW, MIG), duplex stainless steel products. The Heat input and interpass Shielded Metal Arc Welding (SMAW, “matching” fillers have been reported to temperature “stick”), Flux Core Wire Welding (FCW), give acceptable results when joining Submerged Arc Welding (SAW), duplex stainless steels to austenitic and Plasma Arc Welding (PAW). stainless steels or to carbon and alloy Duplex stainless steels can tolerate Oxyacetylene welding should not be steels. relatively high heat inputs. The duplex used because of the associated carbon solidification structure of the weld metal contamination of the weld. Preheating is resistant to hot cracking, much more so than that of austenitic weld metals. Filler metals As a general rule, preheating is not Duplex stainless steels, with higher