Ti-13板材中晶界特征及其对疲劳裂纹萌生与-中国有色金属学报.PDF

20 1 2010 10 Vol.20 Special 1 The Chinese Journal of Nonferrous Metals Oct. 2010 1004-0609(2010)S1-s0429-04 Ti-15-3 1 2 , (1. 114000 2. 110004) Ti-15-3 Ti-15-3 40˚~60˚ 60% 15˚ 4% Ti153 TG 146.23 A Grain boundary characterization and its influence on fatigue crack initiation and propagation in Ti-15-3 sheet SA Shi-yong 1, WANG Ping2 (1. Representative Office of PLA Navy to Anshan Iron and Steel Group Corporation, Anshan 114000, China; 2. Key Laboratory of Ministry of Education for Electromagnetic Processing of Materials, Northeastern University, Shenyang 110004, China) Abstract: The grain boundary characterization and its influence on the fatigue sliding band initiation and short crack propagation in Ti-15-3 sheet were studied. The results show that most of the grain boundaries belong to the large-angle grain boundary, less of them belong to the small-angle grain boundary. In the present statistic scope, the adjacent grains with misoritation angle of 40˚−60˚ are over 60%, the adjacent grains with misoritation angle less 15˚ are about 4%. The fatigue sliding band preferres to initiate near the large-angle grain boundary, which shows the barrier effect on the short crack propagation. And no sliding band is found near the small-angle grain boundary, but the fatigue short crack propagates across easily these small-angle grain boundaries. Key words: Ti-15-3 alloy; cold-rolled sheet; grain boundary; sliding band; fa