电镀产品的检验验标准（Inspection standard of electroplating products）.doc

电镀产品的检验验标准（Inspection standard of electroplating products） General inspection standard of electroplating products The inspection of the plating terminal is the indispensable work after the completion of the electroplating. Only the qualified products can be handed over to the next process. Usually in the inspection items: film thickness (thickness) and adhesion (adhesion), welding (solderability), appearance (appearance), packaging (package). Salt fog experiment (salt spray test), have special requirements for product drawings, there is porosity test (30U ) gold using nitric acid vapor method, palladium plating nickel products (using gel electrolysis) or other environmental test. Film thickness: 1., the thickness of the film is the basic project of electroplating inspection. The basic tool is the fluorescent film thickness gauge (X-RAY). The principle is to use X ray to irradiate the coating, collect the energy spectrum of the coating, and identify the thickness and composition of the coating. 2. use X-RAY notes: 1) spectral calibration is necessary for each startup 2) do cross calibration every month 3) the gold nickel calibration shall be done at least once a week 4) measurement should be based on the steel used in the product selection test files 5) there are no test files for new products, and test files should be established 3. significance of test files: Example: Au-Ni-Cu (100-221, Sn, 4%@0.2, CFP) Au-Ni-Cu---------- test on copper substrate nickel plating, bottoming, and then gold-plated thickness. (100-221, Sn, 4%-------AMP copper, numbered 4% copper with tin) Two. Adhesion: Adhesion test is the basic test of electroplating. Adhesion is not good. It is one of the most common negative phenomena in electroplating. There are two kinds of testing methods: One Bending method: first use copper pad with the same thickness required detection terminal to bending, vise samples will be bent to 180 degrees, with a microscope to observe whether there is bending surface c