工艺因素对超声-挤压过滤法制备β-榄香烯固体脂质纳米粒平均粒径.docVIP

工艺因素对超声-挤压过滤法制备β-榄香烯固体脂质纳米粒平均粒径 　 作者：王艳芝，周欣羽, 郑甲信，毕殿洲，邓意辉 【摘要】 　　目的研究工艺因素对β-榄香烯固体脂质纳米粒（SLN）平均粒径的影响。方法以超声-挤压过滤法制备β-榄香烯SLN，研究超声强度、超声时间以及制备温度等因素对其平均粒径的影响。结果绝大多数β-榄香烯SLN的平均粒径小于150 nm。其平均粒径随超声时间的延长和制备温度的提高而有所下降，但是受持续超声时间的影响较小。考察的制剂中，在超声强度为400W、超声温度为80℃、超声时间为6 min条件下制备的β-榄香烯SLN的平均粒径最小。结论采用超声-挤压过滤法可制备β-榄香烯SLN, 超声强度、总体超声时间以及温度等是影响其平均粒径的主要工艺因素。 【关键词】 工艺因素 β-榄香烯固体脂质纳米粒 超声-挤压过滤法 　　Abstract：ObjectiveTo study the influence of the technological factors on the mean particle size of β-elemene solid lipid nanoparticles(SLN). Methodsβ-elemene SLN were prepared by the method combining sonication and membrane extrusion．Effects of the technological factors on the mean particle size of β-elemene SLN were studied, including sonication strength, total period of sonication length and preparation temperature, etc. ResultsThe results showed that most mean diameter of β-elemene SLNs was less than 150nm. The size of β-elemene SLN decreased with the increase of the total period of sonication length or the preparation temperature, but less influenced by the sonication interval length. Among the detection samples, smaller β-elemene SLN could be obtained at the sonication strength of 400w, with a total period of sonication length of 6min and at 80℃, respectively. Conclusionβ-elemene SLN could be prepared by the method of sonication and membrane extrusion, the technological factors of sonication strength, total period of sonication length and preparation temperature have influence on the particle size. 　　Key words：Technological factor; β-elemene solid lipid nanoparticles； Sonication and membrane extrusion 　　固体脂质纳米粒（SLN）是一种新型的微粒给药体系，对脂溶性药物的包封率较高。由于该剂型采用与机体生理相容的固体脂质为基本骨架材料，给药后的体内毒性与聚合物纳米粒相比大大降低，如处方设计得当，还可拥有药物释放速度可控、物理稳定性高等优点，而且不存在大生产转化问题，因此备受关注［1］。制备SLN的主要方法有高压乳匀法、微乳法和溶剂扩散法等，随着研究的深入，一些新的制备方法不断涌现，如薄膜接触器法和超声-挤压过滤法等［2,3］，其中超声-挤压过滤法是将在超声作用下初步分散的制剂，在高温下挤压通过微孔滤膜的方法，具有操作简单、设备投资少、脂质浓度大、无需有机溶剂等特点，非常适合科研和小型生产性SLN的制备。本文以从中药中提取的脂溶性抗癌有效成分β-榄香烯为模型药物，主要探讨超声-挤压过滤法制备固体脂质纳米粒的工艺因素对其平均粒径的影响。 　　1 材料与仪器 　　1.1 材料 　　β-榄香烯原