沥青路面半刚性基层快速修复材料研究.pdfVIP

10 5 Vol. 10, No . 5 2007 10 JOURNAL OF BUILDING M AT ERIALS Oct. , 2007 : 1007- 62 (2007) 05- 0553- 04 1 2 3 3 马一平 , 谈至明, 陶宇奋 , 郁忠斌 ( 1. , 2000 2; 2. , 2000 2; 3. , 201200) : 采用快凝快硬硫铝酸盐水泥和特种添加剂研制 沥青路面半刚性基层混凝土修复 材料. 研究结果表明: 该材料在30 min 左右凝结硬化, 4~ 5 h 左右抗折强度达 1. 0 MPa 以上抗压强度达10 MPa 以上; 该材料与老的沥青路面半刚性基层材料粘结良好, 并具 有一定的微膨胀性能; 该材料在试验路修复施工中可满足沥青路面半刚性基层快速修复 的要求. : 快凝; 快硬; 快速修复材料; 半刚性基层; 沥青路面; 硫铝酸盐水泥 + : U 414. 1 8 : A Research on Rapid Repairing Material for Semirigid Base of Asphalt Road 1 2 3 3 MA Yi-p i ng , T A N Zh i-ming , T A O Yu-f en , Y U Zhong- bi n ( 1. Key Laborat ory of Advanced Civil Engineering Materials of Ministry of Education, Tongji University, Shanghai 2000 2, China; 2. Key Laboratory of Road and T raffic Engineering of Ministry of Educat ion, Tongji University, Shanghai 2000 2, China; 3. Shanghai Pudong New Area Road Administrative Department, Shanghai 201200, China) Abstract: Concrete repairing material for semirigid base of high-grade asphalt road w ith heavy traffic w as prepared by use of rapid-setting and rapid-hardening surphoaluminate cement and spe- cial additives. The test results show that it can set and harden after about 30 min, and w ithin 4~ 5 h, its flexural and compressive strength can reach more than 1. 0 MPa and 10 MPa respec- tively. T he bond betw een the material and the old semirigid base is quite high. The material can expand a little during its hardening process. The in-site rapid-repairing of semirigid base w ith