砖机配件（Brick machine parts） 95 alumina ceramic head Technical index: The alumina content is more than 95% The volume density of more than 3.5g/cm3 The hardness is greater than or equal to 82HRA The flexural strength is not less than 220Mpa Zirconia alumina product has high hardness, toughness is 3 times that of ordinary ceramic, wear resistance is 10 times of ordinary steel, hard alloy YG6x alloy to 1/4 of the cost, which are made of wear-resistant film. The spray nozzle. The stem, widely used in chemical industry, geology and tile machinery, is a new type of wear ideal material. Specializing in the production of HW brick machine special core rod, the core rod for 65Mn spring steel material. Compared to ordinary core rod more wear-resistant, longer service life. It is the most ideal product of brick machine parts. Name data unit The volume density is 3.24 g/cm3 Porosity 4.2% The average diameter of grain is 8 (m) The calcination temperature is 1350 degrees centigrade Coefficient of linear expansion 5.98-8.0 a (* 10-6/ DEG C) Thermal conductivity 58 w/m.k DC breakdown strength 35 kv/mm Dielectric loss (1-2) * 10-420 1MH2 Dielectric coefficient 9.1 Melting point 2800 DEG C Specializing in the production of HW brick machine special core rod, the core rod for 65Mn spring steel material. Compared to ordinary core rod more wear-resistant, longer service life. It is the most ideal product of brick machine parts. 2, manganese chromium spring steel, long and short brick core rod has good wear resistance, not easy to deformation, use life more than two times higher than cold drawn steel, there are a variety of specifications for users to choose. 3, the company specializing in the production of brick factory (building materials factory) porous brick wear-resistant core head dedicated core rod. This product all adopts GB 65 manganese spring steel production, with high elasticity, good toughness and so on 111111111111111111111111111111111111111111111111111111111111111111 Export ma