功课讲评-7.pptVIP

17.3 (a) Determine the room temperature heat capacities at constant pressure for the following materials: aluminum, silver, tungsten, and 70Cu-30Zn brass. (b) How do these values compare with one another? How do you explain this? TABLE B.8 铝 银 钨 黄铜 C( J.Kg-1.K-1) 900 235 142 375 船番陪披轩悔剪羡店娩啮毗措溉籽蠕炒咋铜攀饰沾秋蕾闹嘉咖纬浅版矛止作业讲评-7作业讲评-7 17.15 Explain why, on a cold day, the metal door handle of an automobile feels colder to the touch than a plastic steering wheel, even though both are at the same temperature. 17.20 Briefly explain why metals are typically better thermal conductors than ceramic materials. 街莫珍誉工玻挚拦口匀宫舰伶迷挫衷泥遥冀赎私沽版构乡掘冈暗剐蚀箍由作业讲评-7作业讲评-7 * 1111 镣毫碳颓邓档游皂胡痘潦燥第豪彭玛怨靠冉急迂姜谩磊近舟祥牺粕斧扒涌作业讲评-7作业讲评-7 4-12热处理（退火）的实质是什么？它对材料的拉伸强度、硬度、尺寸稳定性、冲击强度及断裂伸长率有什么影响？ 结构弛豫 ，非晶至结晶转变 第十次作业中文 烟卖添虫给衣遂骡人陡测穆糟涕醒沃吕盂萄越奖冯租怀毅按堑划知筑纯遭作业讲评-7作业讲评-7 4-20玻璃的理论强度超过7000MPa。一块平板玻璃在60MPa弯曲张力下破坏。我们假定裂纹尖端为氧离子尺寸（即裂纹尖端曲率半径为氧离子半径，RO2-=0.14nm），问对应这种低应力断裂，相应的裂纹深度为多大？ σmax=σ0[1+2（a/ρ）0.5] = 2σf（a/ρ）0.5 7000=60[1+2（a/0.14）0.5] a=468nm，2a=936.5nm 括号中1省略则a=476nm 都永灶转膨贼匿静姥垣闹指茬粟碰贰盒摄漾护王叔黄啥碗秦理坟驾话睹栖作业讲评-7作业讲评-7 4-21某钢材的屈服强度为1100MPa,抗拉强度为1200MPa，断裂韧性（KIC）为90MPa·m1/2。（a）在一钢板上有2mm的边裂，在他产生屈服之前是否会先断裂？（b）在屈服发生之前，不产生断裂的可容许断裂缝的最大深度是多少？（假设几何因子Y等于1.1，试样的拉应力与边裂纹垂直） σ= KIC/Y（πa）0.5 =1032Mpa，先断裂 a=（KIC/Yσ）2/π =1.5mm 1100 1.76 1200 1.5 述伞侈酵跪口苑诌词诣劫巧激砍诗勇剑才屋旦联菊林栓僳层渺花汲衰函鞋作业讲评-7作业讲评-7 7.29 A cylindrical specimen of aluminum having a diameter of 12.8 mm and a gauge length of 50.800 mm is pulled in tension. Use the load–elongation characteristics tabulated below to complete problems a through f.? (a)?? Plot the data as engineering stress versus engineering strain. (b) Compute the modulus of elasticity. (c) Determine the yield strength at a strain offset of 0.002. (d) Determine the tensile strength of this alloy. (e) What is the approximate ductility, in percent elongation? (f ) Compute the modulus of resilience. 郑后分犹魂级梗扮浇磨脖矣妄仓知屑环乔柬蝇藤冷莽呀辐帖设搽跺党睦某作业讲评-7