环氧树脂整体柱的制备和应用 【摘要】：本研究采用环氧树脂作为单体，二乙烯三胺作为环氧树脂的固化剂，聚乙二醇为致孔剂，在内径为1cm,长为10cm的玻璃柱中制备环氧树脂-二乙烯三胺整体柱。详细考察了在确定单体/固化剂比例前提下，改变聚合物混合液中聚乙二醇的含量，确定聚乙二醇含量对整体柱孔径的影响；定性分析整体柱对Cu2+吸附和解吸能力；用扫描电镜观察整体柱的孔隙形态。结果证明：当单体/固化剂为75：25时，聚乙二醇含量为70%，聚乙二醇分子量为1000时，所制备的整体柱具有很好的稳定性和吸附性能。 【关键词】：环氧树脂、整体柱、吸附、Cu2+ 【Abstract】： This research prepared epoxy resin-based polymer monolithic column in 1cm×10cm i.d. glass tube, using epoxy resin as monomer, PEG as poregen, diethylenetriamine as curing agent. In the certain proportion of monomer and curing agent, the effect of the amount of PEG in the mixture on the properties of monolithic columns was researched. The adsorption and desorption of Cu2+ on the monoliths were studied qualitatively. The structure of pores was recorded by SEM. The results show that the prepared monolithic columns have good stability and adsorption capacity. 【Keyword】： Epoxy Resin, Monolithic Columns, Adsorption, Cu2+ 目录 一.绪论 1.1整体柱的发展现状………………………………………………(1) 1.2硅胶基质整体柱…………………………………………………(1) 1.3有机基质整体柱…………………………………………………(2) 1.3.1分子印迹整体柱………………………………………………(2) 1.3.2其它有机基质整体柱…………………………………………(3) 1.4 有机-无机复合基质整体柱……………………………………(4) 1.5铜离子富集和吸附研究现状……………………………………(4) 1.6环氧树脂-二乙烯三胺整体柱吸附铜离子的原理………………(6) 二.实验部分 2.1仪器和设备………………………………………………………(6) 2.2试剂和规格………………………………………………………(6) 2.3整体柱的制备……………………………………………………(7) 三.结果与讨论 3.1 PEG分子量对整体柱的影响……………………………………(8) 3.2 聚合物中PEG含量对整体柱的影响…………………………(8) 3.3固化温度对固化时间的影响……………………………………(9) 3.4 Cu2+离子的吸附实验……………………………………………(9) 3.5 Cu2+离子的解吸实验……………………………………………(10) 3.6 扫描电镜观察整体柱特征……………………………………(10) 3.7 红外光谱分析…………………………………………………(12) 四、结论与展望 4.1 增强环氧树脂-二乙烯三胺整体柱对重金属的吸附能力（13） 4.2 整体柱在电镀废水处理中的应用…………………………（13） 五、参考文献 六、致谢 七、附录 附录一 文献综述 整体柱的现状与发展…………………………（17） 附录二 译文一 分子印迹整体柱在色谱分离中的应用………………（22） 译文二 用固体发泡剂和超声波制备组织工程用无溶剂介入的聚合物的方法……………………………………………（28） 译文原文一 Monolithic Molecularly Imprinted Columns for Chromatographic Separation…………………………（） 译文原文二 A method for solvent-free fabrication of porous polymer using solid-state foaming and ultrasou