TA2内绝热剪切带的微观组织演化机制探讨.pdfVIP

_______________________________________________________________________________ Microstructure evolution mechanism in adiabatic shear band in TA2 1 1 2 YANG Yang(杨扬) ，XIONG Jun(熊俊) ，YANG Xu-yue(杨续跃) (1. School of Materials Science and Engineering, Central South University, Changsha 4 10083, China; 2. Dept . of Mechanical Engineering and Intelligent Systems, The University of Electro-Communications, Japan) Abstract : The microstructure evolution mechanism in adiabatic shear band in commercial pure titanium (TA2) . 5 6 at high strain rate ( g ≈10 ~ 10 /s) were studied. The nanosized recrystallized grains (about 50 nm in diameter) within the center of adiabatic shear band (ASB) were observed by means of transmission electronic microscope (TEM). A Rotational Dynamic Recrystallization (RDR) mechanism can explain the microstructure evolution (ie. nanosized grains was formed within 5-10 μs) in ASB. Kinetics calculations indicated that the recrystallized small grains were formed during the deformation and didn t undergo significant growth by grain boundary migration after deformation. Key words: shear band; microstructure evolution; dynamic recrystallization CLC number: TG146.2 Document code: A During the past decade, the microstructure result of kinetic calculation showed that the grain with characteristic of adiabatic shear band (ASB) was diameter sm