浅谈钢筋混凝土结构裂缝产生原因和防治措施.doc

浅谈钢筋混凝土结构裂缝产生原因和防治措施 　　摘要：随着城镇化的不断推进，高层建筑如雨后春笋般出现，建筑工程中混凝土工程的体量不断增大，预拌混凝土是当前最广泛使用的建筑结构材料之一。然而，由于各种各样的因素，包括人为因素、原材料因素、施工工序等因素，混凝土裂缝在建筑工程中已经成为最常见的质量通病。结合一些观察和实际经验，对钢筋混凝土结构裂缝产生原因、防治对策进行了浅显简要地分析。 关键词：高层建筑 ；钢筋混凝土结构 ；裂缝； 原因 ；防治 Abstract: With the constant promotion of the urbanization, high-rise buildings such as bamboo shoots after a spring rain as there are, in the concrete construction volume increases, the ready-mixed concrete is one of the most widely used construction materials. However, due to various factors, including human factors, material factors, construction process and other factors, concrete crack has become the most common quality problems in construction engineering. Combined with some observation and actual experience, reason, countermeasure of prevention and control of cracks in reinforced concrete structure was simple brief analysis. Key words: high-rise building; reinforced concrete structure; crack; reason; prevention 中图分类号：TV543+.6 文献标识码：A文章编号： 一、钢筋混凝土结构裂缝的主要特征 通过对剪力墙裂缝的观察、总结，主要有以下特征：绝大多数是竖向裂缝，多数裂缝长度接近墙高，两端逐渐变细而消失；裂缝数量较多，宽度一般不大，超过0．3mm的很少，大多数裂缝不大于0．2mm；裂缝出现时间多在拆模后不久，有的还与气温骤降有关；随着时间裂缝继续发展，数量增多，但缝宽增大不多；地下室墙沿长两端附近裂缝较少，中部及附近较多。地下室回填后常见裂缝处渗漏水，但水量一般不大。 通过对板面裂缝的观察、总结，主要有以下特征：裂缝一般较短，不超过1米长，大多数在300—600mm间；裂缝数量较多，宽度大约在0．5-3mm左右；裂缝分布一般在次梁所围成的方框内，有些沿板筋分布。有些裂纹呈不均匀分布；在楼板角部产生贯穿性的斜裂缝，与纵横墙形成约45度的夹角；在楼板跨中区间内，线管予埋处、后浇板带、以及施工缝处出现通长贯穿性的裂缝；单块面积大的楼板裂缝现象多于单块面积小的楼板。 二、钢筋混凝土结构裂缝产生的主要原因 混凝土在凝固过程中，随着混凝土中水分蒸发、湿度降低、体积减少，而产生收缩变形。如果混凝土构件中收缩受到限制，则混凝土内会产生拉应力，住宅现浇楼板角部受到纵横两个方向上下墙体或梁柱构件的约束，并在角部合成一个主拉应力，当主拉应力超出楼板混凝土极限抗拉强度时，楼板就将产生与主拉应力方向垂直的切角斜裂缝，且裂缝贯穿楼板。在楼板跨中预埋通长线管处、后浇板带处、施工缝处是楼板混凝土截面抗拉能力最薄弱处，当楼板混凝土产生收缩变形时必然先在上述部位产生裂缝，由此可见，混凝土收缩变形是产生上述裂缝的主要因素。 混凝土具有热胀冷缩、湿胀干缩的特性，尤其是在浇筑混凝土时气温较高，其混凝土冷却收缩变形同干缩变形一样也会在板内产生拉应力，当其最不利因素组合在一起时，更易产生楼板裂缝。 材料方面因为商品混凝土水泥用量大、含砂率大、石子粒径小、塌落度大，商品混凝土虽然渗入了外加剂，但因其可泵性、坍落度的需求以及含砂率大等情况，不能减少水泥用量和水的用量，因此商品混凝土的收缩性比较大。 有些设计以采用后浇带的形式来替代伸缩缝的设置，后浇带主要是解决主体结构在施工期间的混凝土收缩变形，后浇带的间歇时间只有二个月左右，甚至更短而在后浇带完成后继续存在混凝土的收缩变形。予埋的线管均为PVC管，有些通长管是通过跨中单层配筋处，由于PVC管与