矿物掺合料对橡胶集料水泥砂浆强度影响.docVIP

矿物掺合料对橡胶集料水泥砂浆强度影响 　　[摘要]： 本文研究了粉煤灰、矿渣单掺和双掺时的掺量对橡胶集料水泥砂浆28d强度的影响，试验结果表明，单掺粉煤灰和矿渣掺量均在10%以内时，砂浆的抗压、抗折强度比未掺矿物掺合料时均能得到较大提高。从改善砂浆韧性来看，单掺矿渣比单掺粉煤灰的效果要好。粉煤灰与矿渣以不同比例双掺时的效果要优于单掺时，其中粉煤灰掺量15%、矿渣掺量10%时，砂浆的韧性最好。 [关键词]：矿物掺合料 橡胶集料水泥砂浆 抗压强度 抗折强度 中图分类号：TQ172文献标识码： A The Influence of Mineral admixtures on Strength Of Crumb Rubber Cement Mortar JIANG Li1，XUE Gang 2，WANG Wei-hua2 (1.Department of Mechanical and electronic engineering, Bengbu college, Bengbu 233030, China;2. Architecture and Civil Engineering School, Inner Mongolia University of Science and Technology, Baotou 014010, China) Abstract: This paper studies the fly ash and slag when single or mixed content on the influence of crumb rubber cement mortar?s strength of 28 d. The experimental results show that single dosage offly ash or slag were less than 10%, the compressive strength and flexural strength of mortar can be improved greatly than without adding mineral admixtures. From the point of improve the toughness, single mineral slag is better than the effect of single mixing fly ash. The effect of fly ash and slag mixed with different proportion of double is superior to single mixing, one of the 15% dosage of fly ash and slag content is 10%, the toughness of the mortar is best. Key words: Mineral admixtures Crumb rubber cement mortar Compressive strength Flexural strength 1引言 近年来，粉煤灰、矿渣微粉等矿物掺合料因为各自在化学成分、细度、颗粒形态之间的不同差异，在应用中呈现出很多不同的效果，已成为制备高强砂浆（混凝土）不可缺少的组分。有研究证明，矿物掺合料的应用在节约水泥、废物利用、带来明显经济效益的同时，粉煤灰的加入可以提高砂浆（混凝土）的后期强度，和易性好，可改善水泥基体的孔结构，提高其密实性，抗硫酸盐腐蚀性好[1,2]等优点，掺矿渣微粉的砂浆（混凝土）的早期强度较高，但其减水效应不及粉煤灰，掺量过大时，砂浆（混凝土）后期收缩较大，容易开裂[3]。如果能将粉煤灰和矿渣微粉两种性能各异的矿物掺合料同时掺入到水泥砂浆中有可能相互激发、相互补充，产生一定的叠加效应。另有研究表明，若胶凝材料颗粒能形成良好的级配，可彼此紧密填充，从而降低水泥浆体的空隙率，改善孔结构，对砂浆（混凝土）的性能起到改善 作用[4,5]。 本文针对在建筑材料领域中尚缺少矿物掺合料对橡胶集料水泥砂浆性能影响的研究这一现状，进行了单掺粉煤灰、单掺矿渣微粉、粉煤灰和矿渣微粉双掺时对橡胶集料水泥砂浆强度影响的试验，从而得出粉煤灰和矿渣微粉合理的掺量范围。如能得到理想的结果，将为矿物掺合料在橡胶集料水泥砂浆工作性能、耐久性等方面的研究打下良好基础。 2试验概况 2.1试验原材料 水泥采用内蒙古草原牌P.O42.5普通硅酸盐水泥； 砂子为细砂，堆积密度为1 592 kg/m3，含泥量为8.9%，细度模数为2.2；