铝合金管道焊缝射线检验工艺研究及缺陷评定.PDF

第26 卷第5 期 无损检测 Vol . 26 　No . 5 2 0 0 4 年 5 月 ND T May 　2 0 0 4 试验研究 铝合金管道焊缝射线检验工艺 　 研究及缺陷评定 郭伟灿 ,马夏康 毛建军 　 ( ) ( ) 浙江省特种设备检验中心 ,杭州 　310020 　　 杭氧液空有限公司 ,杭州 　310015 摘　要 :分析了铝合金管道焊缝射线检测主要技术特点 ,进行了提高照相灵敏度的工艺试验 和研究 ,介绍了铝合金管道焊接中经常产生的缺陷影像特征及评定方法。 关键词 :射线检验 ;铝合金管道 ;焊缝 ;缺陷 　　中图分类号: TG115. 28 　　　文献标识码 :A 　　　文章编号 (2004) STUDY ON RADIOGRAPHIC TESTING TECHNOLOGY OF WELDING SEAMS IN AL UMINIUM ALLOY PIPE AND THE DEFECT EVAL UATION GUO Weican , MA Xiakang (Zhejian g Special Equipment Inspection Centre , Hangzhou 310020 , China) MAO Jianjun ( Hangyang Air Liquid Limited Corporation , Hangzhou 310015 , China) Abstract: The technology characters of radiographic testing for welding seams in aluminum alloy pipes were analyzed , testing and researches on improving the radiographic sensitivity were performed , and the image character and its evaluation method of the defect which often occurred in aluminum alloy pipes welding were simply introduced. Keywords :Radiographic testing ; Aluminum alloy pipes ; Welding seam ; Defect 　　目前 , 国内空分设备冷箱内管道主要采用国产 验研究 ,并在工程实践中取得了良好效果。 L F 系列铝合金材料 ,管道对接焊缝普遍采用手工钨 1 　铝管道焊缝射线检测主要技术特点 极氩弧焊。因铝的导热系数和线膨胀系数分别为钢 的四倍和两倍 ,焊缝凝固时体积收缩率达 6. 6 % ,加 ALC 空分项目冷箱内铝合金管道壁厚为 4 ～ ( 上铝的高温强度低 ,塑性差 在 640 ～656 ℃伸长率 12mm ,管子直径为 57 ～508mm ,铝材料生产标准 0. 69 %) ,使铝焊缝在较高的焊接应力作用下容易