包覆芦荟微胶体的高分子烧烫伤敷料之研制DevelopmentofPolymeric.PDFVIP

南台科技大學學報第 34 卷第 4 期 ‧2009 年 12 月 1 包覆蘆薈微膠體的高分子燒燙傷敷料之研製 鄒國鳳 元培科技大學生物醫學工程系 助理教授 摘 要 本篇研究是以蘆薈膠體與羥基甲基丙烯酸乙酯為原料，利用交聯聚合與材料之澎潤特性來製作可應 用於燒燙傷治療的複合材料。蘆薈膠體可透過膨潤過程進入多孔性的高分子基材中。這項研究並利用光譜 儀與光學顯微鏡分析複合材料的微結構與成分。材料之親水性、保濕性與透氣性也利用實驗測得，其飽和 水含量可達 48% ，透氣性亦高達99% 。實驗結果顯示，這些特性均優於市售之人工皮膚。 關鍵詞：蘆薈膠體、羥基甲基基丙烯酸乙酯、燒燙傷敷料 Development of Polymeric Dermal Wounds Dressing Contained Aloe Vera Gel Kuofeng Chou, Assistant Professor Department of Biomedical Engineering, Yuanpei University Abstract The swelling behavior of poly(hydroxyl ethyl methacrylate) and crosslinking polymerization are applied to fabricate a novel composite material with aloe vera for the application of wounds dressing. Aloe vera transports into porous polymeric matrix through swelling process. The microstructure and composition of the composites are analyzed by using UV-Vis spectrophotometer and optical microscope. The hydrophilic property, water loss rate and permeability of materials are measured in this study. The equilibrium water content of this material is 48% and permeability is 99%. The result shows that these characteristics are more excellent than commercial artificial skins. Key words: aloe vera, Poly(hydroxyl ethyl methacrylate), Wounds dressing 壹、簡介 由蘆薈葉所萃取的膠體已被證實具有各種藥性，特別是具有癒合燒燙傷與凍瘡、抗菌、抗發炎、降 低血糖及保護消化道等功效(Reynolds T. Dweck A. C., 1999; Davis, R. H.等人 1992; Chithra P., 1998), 。在 燒燙傷癒合部分即包括三項作用：(1)抗感染(2)新組織形成(3)基質重建。關於蘆薈萃取膠質的研究已有多 項動物實驗及燒燙傷癒合有關的蛋白質因子被報導(Chithra P. 等人, 1998; Davis R. H. 等人, 1989; Lee M. J. 等人, 1998) 。這些研究顯示，蘆薈萃取膠質能夠刺激芽母細胞成長、加強傷口張力強度及傷口組織的 膠原蛋白再生。同時，蘆薈膠還能夠藉著增加乙醛(aldehyde)含量和