ZnS薄膜的制备及摩擦学性能的研究.pdfVIP

Material Sciences 材料科学, 2014, 4, 152-157 Published Online July 2014 in Hans. /journal/ms /10.12677/ms.2014.44023 Fabrication and Tribological Performance of ZnS Film 1 2* Weiqi Wan , Shuyan Yang 1 Qingdao No. 1 Middle School, Qingdao 2 School of Mechanical Engineering, Qingdao Technological University, Qingdao * Email: yangshuyan@ th rd nd Received: May 20 , 2014; revised: Jun. 23 , 2014; accepted: Jul. 2 , 2014 Copyright © 2014 by authors and Hans Publishers Inc. This work is licensed under the Creative Commons Attribution International License (CC BY). /licenses/by/4.0/ Abstract ZnS is an effective solid lubricant because its close-packed hexagonal layered structure and low interlayer shear force. In this paper, zinc sulfide films are directly fabricated on zinc substrate through a one-step hydrothermal method. Zinc is used as both zinc source involved in the hydro- thermal reaction and the support for zinc sulfide film. The structure and morphology of ZnS film on zinc substrate are characterized by X-ray diffraction and scanning electron microscopy. The friction properties of ZnS film in dry sliding were observed. The results showed that ZnS film is composed of micro/nano particles with 0.5 μm, providing effective friction-reducing for the zinc substrate under dry sliding contact. Keywords Hydrothermal Method, Zinc Sulfide, Tribological Performance, Friction-Reducing, Wear Protection Performance ZnS薄膜的制备及摩擦学性能的研究 1 2* 万纬祺 ，杨淑燕 1山东省青岛第一中学，青岛 2青岛理工大学机械工程学