水泥基渗透结晶型防水剂在地铁应用的试验研究.docx

水泥基渗透结晶型防水剂在地铁应用的试验研究刘 行 1, 殷素红 1, 2, 李铁锋 1, 文梓芸 1, 2, 史海欧 3, 刘健美 3( 1. 华南理工大学 材料科学与工程学院, 广东 广州 510640; 2. 华南理工大学 特种功能材料教育部重点实验室, 广东 广州 510640;3. 广州市地下铁道设计研究院, 广东 广州 510010)摘 要:Penetron A dm ix 是一种在混凝土拌和时加入的新型水泥基渗透结晶型本体防水添加剂。采用广州地铁工程混凝土所使用的原材料和配合比, 在试验室研究了添加 Penetron A dm ix 后对混凝土性能的影响。结果表明: 掺入一定量的 Penetron A dm ix 后, 混凝土拌合物的流动性能提高; 硬化混凝土的抗渗性能显著提高, 渗透压力比大于 267% ; 抗压强度也有所提高; 但混凝土收缩值比基准混凝土稍大。裂缝自 修复试验表明掺入 Penetron A dm ix 的混凝土试件在水或潮湿条件下确实具有裂缝自修复功能。关键词: Penetron A dm ix 防水剂; 混凝土性能; 渗透压力比; 裂缝自修复中图分类号:TU 528.042.6文献标志码:A文章编号:1002-3550-( 2007) 04-0040-04Experim entalresearch ofcem entitious capillary crystalline w aterproofing m aterialapplied tom etro engineering concreteLIU Hang1, YIN Su-hong1, 2, LI Tie-feng1, WEN Zi-yun1, 2, SHI Hai-ou3, LIU Jian-mei3( 1. College of MaterialsScience and Engineering, South China Universityof Technology, Guangzhou 510640, China;2. Key Laboratory of Specially Functional Materials, Ministry of Education, South China Universityof Technology, Guangzhou 510640, China;3. Design Institute of Guangzhou Metro Coporation, Guangzhou 510010, China)A bstract: Penetron Admix is a new type of cementitious capillary crystalline waterproofing ( CCCW) material which was added in concretemixture. The effect of adding Penetron Admix on the performance of concrete which was manufactured in the same raw materials and mix propor- tion as Guangzhou metro engineering concrete was studied. The results show that , comparing with blank specimens, the flowability of fresh con- crete is improved, its impermeability is obviously increased and the penetration pressure ratio is more than 267% , and its compressive strength is also augmented, but the shrinkage ratio is somewhat greater than blank concrete. The crack autogenous healing test has demonstrated that the con- crete with Penetron Admix have the ability to autogenously heal a crack in water or moisture condition.K ey w ords: Penetron Admix waterproofing material; performance of concrete; pen