自密实钢筋砼钢筋锈蚀和渗透性检测-中国科技论文在线.pdfVIP

中国科技论文在线 中图分类号：TQ172 文献标识码：B 文章编号：1007-0389(2008)04-73-05 自密实钢筋砼钢筋锈蚀和渗透性检测 谭志催 ，李 悦 ，霍 达 ，王永焕2 (1．北京工业大学建工学院，北京 100022；2．中冶集团建筑研究总院，北京 100088) 摘 要：自密实钢筋砼 (SCC)是近年砼界研究热点，但很少有人研究其耐久性。砼中钢筋的抗锈蚀能力和抗渗性是衡量砼 耐久性的重要指标。作者试验配制了强度等级在C30～C60之间的自密实钢筋砼构件，研究测试了SCC构件在不同氯离子环 境下钢筋的抗锈蚀能力，并测试了SCC构件的渗透性。测试结果表明：所研配的自密实钢筋砼具有很好的抗锈蚀能力和抗 渗性 从而得出SCC具有很好的耐久性。 关键词：自密实砼；钢筋锈蚀；渗透性；耐久性 Testing of SCCs reinforcement corrosion and penetrability Tan Zhicuil，Li Yuel，Huo Dal，Wang Yonghuan2 f1．Tlhe college of architecture and civil engineering，Beijing University of Technology，Beijing 100022，2．Central Research Institute of Building and Construction under MCC Group，Beijing 100088) Abstract：SCC is a hot topic of stuay in concrete，however，there are few papers research SCCs durability．Both reinforcement corrosion and penetrability are very important items in the judge of concrete S durability．The paper make SCC components between C30 and C60 ． and research their reinforcement corrosion under different environment．What S more，the paper tests SCC S penetrability．Testing result indicate that SCC is good job at reinforcement CO1TOSiOn and penetrability，SO SCC is well at durability． Key words：self-compacting concrete；reinforcement corrosion；penetrability；durability． 1 砼耐久性问题及其自密实钢筋砼概念 国等一些国家就发现tzl20世纪50年代以后修建的 砼工程设施，尤其是使用在恶劣环境下的砼桥面板 自19世纪20年代波特兰泥问世以来，砼大量 结构．出现病害甚至损坏的现象比20年以前建造 地应用于工程实践。起初，人们认为砼是良好的耐 的结构还要严重。据Mehta教授1991年的报道[3]： 久性材料．是无比坚固．不会自然损坏和失效的。 在桥梁方面，已有253 000座桥的桥面板不同程度 但随着砼的大量使用，使着时间的推移，在世界各 地老化．且每年以35 000座递增．仅维修桥面板 国，许多砼结构出现各种各样严重的破坏现象，到