采用电位法测量混凝土中可溶离子含量的研究.doc

采用直接电位法检测混凝土中可溶离子含量的研究 范文涛1 ，戴民2 ，宁柱伟1 （1.辽宁省建设科学研究院，沈阳 110005） (2.沈阳建筑大学材料科学与工程学院，沈阳 110168) 摘 要:本文论述采用直接电位法检测混凝土中可溶离子含量的测试原理、方法、过程，并以测试钠离子含量为例，与火焰光度计法进行比较，测试的结果准确度高，过程操作简便，测试范围广，易于在实际工作中推广应用。 关键字: 直接电位法；可溶离子；能斯特方程；电位曲线；电极 Studies on Detecting the Content of Dissoluble Ions in Concrete by Direct Potential Method Fan Wentao1 ，Dai Min2 ，Ning Zhuwei1 (1. Construction of Science Research Institute of Liaoning Province) （2．School of Material Science and Engineering , Shenyang Jianzhu University,Shenyang 110168） Abstract: The theory, means and process about detecting the content of dissoluble ions in concrete by direct potential method were discussed. Comparing with flame photometry in Na+ content detecting, the direct potential method was more accurate, simpler and more accommodative, and will be easy to be promoted and used in reality occasion. Key words: direct potential method, dissoluble ion, Nernst equation, potential curve, electrode 1 引言 在混凝土建筑工程检测过程中, 我们经常遇到混凝土裂缝、变色、膨胀等破坏现象，为了能够找出混凝土的破坏原因，除了对混凝土外部条件进行分析外，还需要对混凝土内部的一些可溶的离子含量进行分析，比如氯离子、钾离子、钠离子、镁离子等，将内外因素相结合，才能更准确判断混凝土破坏的原因，提出合理的解决方案。 测定混凝土中可溶离子含量目前没有统一的国家标准方法，我们在检测过程中采用直接电位法测量，通过已知样品分析、不同仪器测试结果比对等手段，发现采用直接电位法测量较为准确、方便，可以做为混凝土中可溶离子含量测定一种可行的方法。 2 测试原理 采用直接电位法测定混凝土中可溶解的离子含量，利用离子选择电极和参比电极对被测量溶液中待测定的离子进行测量，把被测离子的活度表现为电极电位，不同的离子活度，电极产生的电位不同，在一定离子强度时，活度又可以转化为浓度，从而实现分析测定。 该测试方法的理论依据为能斯特方程（1），公式如下。从公式中可见，离子电极在溶液中所产生的电位与被测离子的活度呈线性关系，测得电位即可通过公式算出离子浓度。 （1） 式中：E—离子电极在溶液中所产生的电位（V）； E0—电极系统的截距电位，在一定条件下可看作一常数（V）； R—气体常数（8.314J ·K-1·mol-1）; T—液体的绝对温度[（273.15+t）k]； F—法拉第常数（96487C·mol-1）； n—离子价数； ±—正号和负号分别对应于阳离子和阴离子； ax—被测离子的活度（g/l）。 3 本实验方案中采用的仪器设备 本实验以测试硬化混凝土中的钠离子为例，需要的仪器设备有：微机离子计(分辨率0.001mg/l);自动控温电磁搅拌器; 217型双盐桥饱和甘汞电极;102型钠电极；火焰光度计；温度计等。 电位法测试仪器安装示意图，见下图1。 图1 仪器安装示意图 1电极（217型双盐桥饱和甘汞电极;102型钠电极）；2容器（盛待测样品溶液）；3自动控温电磁搅拌器；4微机离子计 4 测试前的准备工作 4.1配置标准溶液 制取无钠水，采用蒸馏水或电参水通过离子交换柱，再用石英亚沸蒸馏器进行二次蒸馏，所提取的无钠水用聚乙烯容器隔绝空气保存，备使用。 称取11.7g已于250℃～350℃烘过2h的氯化钠（基准试剂），精确至0. 1mg，置于烧杯中，加无钠水溶解后