马氏体不锈钢水轮机叶片铸造缺陷修补工艺研究.pdfVIP

学兔兔 马氏体不锈钢水轮机叶片铸造缺陷修补工艺的研究 李红霞，柏长友，杨 保 (共享模具有限公司，宁夏 银川 750021) 摘要：针对ASTM A74 3 CA6NM马氏体不锈钢水轮机叶片的铸件特点，对铸造缺陷的焊接修补工 艺进行具体研究和分析。选用牌号为E41 ONiMo一1 5马氏体不锈钢作为焊接材料，严格按照焊接 工艺要求进行操作并合理控制焊后热处理温度。结果表明，该铸件的焊接修补工艺达到技术要 求，焊补合格率达到9 5％以上。 关键词：马氏体不锈钢；水轮机叶片；焊接工艺；焊后热处理；手工电弧焊 中图分类号：TG444 ．1 文献标识码：A 文章编号：1673-3320(2015)05-0027-03 Study on Repairing Process of Casting Defects for Martensitic Stainless Steel Turbine Blade Ll Hongxia，BAI Changyou，YANG Bao (KOCEL Pattern Co．，Ltd．，Yinchuan 750021，Ningxia，China) Abstract：In view ofthe characteristies ofASTM A743 CA6NM martensitic stainless steeI turbine blade casting，specific research and analysis have been carried out on welding repair technology for casting defects．E4 1 0NiMo一1 5 martensitic stainless stee1 was selected as welding materia1．welding process in strict accordance with the requirements was operated，and the heat treatment temperature was controlled reasonably．The results show that the welding repair process of the casting can meet the technical requirements．and the qualified rate of welding repair iS more than 95％． Key words：martensitic stainless steel；turbine blade；welding process；post weld heat treatment；manual arc welding 近十几年来，随着我国水力资源的开发利 1 ASTM A743 CA6NM铸钢的化学成分 用，大型水电机组不断涌现，而大型水轮机叶片 及力学性能 铸件是大型水电机组开发和利用所必须的重要 各水电设备制造商的规范中没有明确对焊接 基础部件川，其用钢一般为ASTM A743 CA6NM 区域金属的力学性能作出要求，焊接区域技术指 (zG06Cr13Ni4Mo)，属于马氏体不锈钢材料系列。 标设计以母材ASTM A743 CA6NM铸钢化学成分 目前，国内各铸造企业在水轮机叶片铸造生产过程 和力学性能为参考目标，其化学成分和力学性能 中，由于工艺、操作等原因，铸件本体不同程度地