制鞋业标准流程之--组底篇.pptVIP

大底/中底/飾片的組合ASSEMBLY O/S M/S BOTTOM DéCOR 1. 大底/中底前段處理O/S M/S PRETREATMENT * * 大底組的任務是把所有底部配件組合成整體的底:It’s task of bottom assembly to make all bottom components into one unite.1.底部依材質分為PU底,橡膠底,EVA M/D底,PVC底…等等,不同材質需用不同的藥水處理,後刷相應的膠水,貼合.According to the bottom material difference, there are rubber sole / PU sole / EVA sole / pvc sole … ect. Different kind sole need be treated with different primer glue then attach into one unite. 現在橡膠底大都是由天然的橡膠(從橡膠樹上取得的)或合成的橡膠制成,,不過他們有相似的性能,比如硬度/彎曲率/防水性.其廣泛應用天從事重活或一般活動所需鞋類Now most of rubber sole are made from the natural rubber that obtained from rubber trees or synthetic rubber. But they have the similar properties example for hardness / flexible / waterproof….They are used in a wide variety of footwear from heavy duty to general purpose.EVA是運動鞋常用到的大底和中底材料,其比橡膠輕,也有彈性及好的絕緣性,與橡膠一樣耐磨.EVA are generally used in sport shoes as outsole midsoles due to it’s lighter than rubber but still has flexible resilient ,and same durability.Pu 底其較輕,但耐磨性比橡膠及EVA底,運動鞋很少用到.Pu sole are used in sport shoes less than rubber eva due to the durability not very good. 1,大底需經過打粗水洗後才進行藥水處理. O/S橡膠用白色1016A+1%B粉;雜色用1016A+2-3%B粉; White rubber O/S primer with 1016A+1%B;varied color rubber do with 1016A+2-3%; EVA需先經過藥水處理,白色用UV-11N,黑色用UV-8N,再過烘箱時間4分鐘,溫度50度,蓋日期章後,過冷凍箱溫度0-5度,時間4分,最後經過UV照射:白色:052J/CM2,黑色:0.47J/CM2,時間:10-12秒. EVA need treat with primer, for white EVA light with UV-11N,for black EVA with UV-8N;put through oven with temperature 50 time 4 minutes ,then put through cooling after stamp the date, at last treat with light ,for white eva , power 052J/CM2 time 10-12sec ;for black eva, power 0.47J/CM2 time 10-12sec. Shank用111YCN+2%RFE藥水處理 Primer O/S: White rubber with 1016A+1%B;varied color rubber with 1016A+2-3%B;EVA with UV light. Primer Shanks with 111YCN+2%RFE. 2.在處理藥水過程中﹐藥水不可太少或過量﹐不可有外溢現象。處理後 During primer, don’t apply the primer too much or too little or come out . 3. 粘藥水的絲瓜布要經常更換. The towel gourd cloth soaked primer need be changed often.