石油树脂对氯化丁基橡胶阻尼性能的影响.docVIP

石油树脂对氯化丁基橡胶阻尼性能的影响 肖方一张喜亮李慧吴驰飞o (华东理工大学材料科学与工程学院上海200237) Effect of Petroleum Resin on the Damping Properties of Chlorinated Butyl Rubber Xiao Fangyi Zhang Xiliang Li Hui Wu Chifei (Ea,日t China University of Science and Technology，Shanghai，200237) 摘要l本文通过石油树脂同氯化丁基橡胶共混，制备了一系列性能优良、价格低 廉的新型阻尼材料。本研究着重考察了石油树脂软化点及添加量对阻尼材料性能 的影响。材料的DMA结果表明，氯化丁基橡胶和石油树脂的共混物是相容体系， tan占峰随石油树脂软化点温度的提高而依次向高温方向偏移；另一方面，随石油树 脂含量的增加，材料的tan 6峰依次向高温方向偏移，并且tan 8峰值也随之提高。， 关键词 氯化丁基橡胶 阻尼 石油树脂 Abstract The effects of petroleum resins on the damping pmper[ies of chlorinated bull rubber(C1一 IR)were investigated by dynamic mechanical analysis As to the binary systems of CIIR／petroleum resins．they show a single tan 8 peak associated with CIIR，and its peak location shifts to higher tem peratures with increasing the softening points of the petroleum resins，this behavior shows that petmle— am resins are compatible with CIIR．On the other hand，in case of the effect of petroleum resin content on the damping properties．It w∞found that with increasing the P／0 content．the maximum value of the tan 8 peak also increase and its peak location shifts to higher temperatures．So CIIR／petroleum res- ins system is a high-performauce damping material． Keywords chlorinated butyl rubber，damping，petroleum resin 1弓I言 随着人们对生活环境舒适性要求的提高以及军工产业的需求，阻尼材料的研发受到很 多研究人员的关注。制备高分子阻尼材料的方法主要有共混 、IPNsⅢ和高分子与有机小 分子杂化Ⅲ技术。共混法仅仅局限于高聚物与高聚物之间的共混，而高聚物与低聚物共混 制备阻尼材料的方法鲜有报道。 本研究主要采用氯化丁基橡胶(CIIR)与石油树脂共混，制备了综合性能优良的阻尼材 ●吴驰飞：电话：021电子信箱：wucf@ecusL edu vii  L新型高分子材料 料。石油树脂常被用于胶黏剂的工业生产中，其增黏效果也是缘于与聚合物共混后在材料 玻璃化转变区间具有较大的滞后，这同阻尼材料的特点相同。另外石油树脂还具有价格低 廉、同橡胶材料相容性好、热稳定性好、黏性好等优点，所以本研究尝试将石油树脂用于阻尼 材料设计与制备中。 2实验部分 2．1主要原料 氯化丁基橡胶(CIIR)：HT-1066，美国埃默森公司；石油树脂：日本荒JiI化学工业株式会 社，P后面的数字代表石油树脂软化点。 2．2样品制备 在双辊开炼机上，首先塑炼氯化丁基橡胶，然后DIA．石油树脂混炼8 min，混炼均匀后下片。 物料在2lnln厚的模具中，在150。C、10MPa条件下热压10min，冷却制备测试阻尼性能的试样。 2．3动态力学性能测试 材料的动态力学性能测试使用日本UBM公司Rheogel E4000型动态机械分析仪(DMA) 果用拉伸模式，样品尺寸为20 mm x5 mm×2 mm，频率为11 Hz，升温速率为3℃／IIlin。 3结果与讨论 3．1 氯化丁基橡胶的阻尼性能 首先通过DMA测定了原料氯化丁基橡胶