原位反应喷射沉积7075铝合金的塑性变形机理.PDFVIP

58 / 2007 9 7075 Plast ic Def orm at ion M echanism of I n-s it u React ive Spr ay Form ed 7075 A l A lloy 1 2 1 , , ( 1 , 010051 2 , 010020) 1 2 1 LIU H u-i min , H unu sit u , Y O U Guo- yan ( 1 Schoo l of M at erials Science and Engineering, Inner Mong olia U niversit y of T echnolo gy, H uheh aot e 010051, China 2 Physics and Elect ronic Inf orm at ion Col leg e, Inner M ongo lia N orm al U niversit y, H uheh ao te 010020, China) : T iC / 707 5 , T iC / 7075 P P - , : , 4 00 e , 4 50 e , : 7075 : T G 14 61 2 : A : 100 1- 43 81( 2007) 09- 005 8-04 Abstract: T he plast ic def orm at ion beh avior of in-s i tu react ive spr ay for med 707 5 A l alloy during hot com pres sion def ormat ion w as st u died by isot herm al com pression test at Gleeble- 1500 t herm a-l mechan- ical simulato r1 T he dynam ic recr yst allizat ion mech anism during hot co mpres s w as ex amined using SEM and the t ru e st ress- str ain curves1 T he result s show th at the f low st ress decr eases w it h t he in- crease of defor ming t em perat ure, dynamic recryst al liz at ion occurs at 4 00 e of def orming t emp er at ure. When t he defor mation t emp erat ure incr eases to 450 e , t he balance is remained bet w een hardening and sof t ening dur ing