锂离子电池阻燃剂的研究.pdfVIP

锂离子电池阻燃剂的研究 贺艳兵 唐致远 陈玉红 刘强 (天津大学化工学院应用化学系 天津 300072) 摘要：测试了三种阻燃剂磷酸三（β-氯乙基）酯（TCEP ）、磷酸三苯酯（TPP ）和磷酸三甲苯 酯（TCP ）分别对电解液 1mol/L LiPF6/EC+DMC (1:1 质量比)的阻燃效果，并研究了 5wt% 阻燃剂分别对 18650 型石墨/LiCoO2 电池的电化学性能的影响；结果表明三种阻燃剂都具有较 好的阻燃效果，其中磷酸三苯酯阻燃性最好，但对电池电化学性能的影响TCEP最小。综合考 虑TCEP是一种相对较好的阻燃剂。 关键词：阻燃剂；磷酸三（β-氯乙基）酯（TCEP ）；磷酸三苯酯（TPP ）；磷酸三甲苯酯（TCP ） The Research of Flame-retardant Additives for Lithium-ion Batteries HE Yan-bing ，TANG Zhi-yuan, CHEN Yu-hong, LIU qiang (Department of applied chemistry, school of chemical engineering, Tianjin University, Tianjin 300072) Abstract: The flame-retardant effects of Tri(β-chloroemethyl) phosphate (TCEP), Tripheyl phosphate (TPP) and Trieresyl phosphate (TCP) respective for the electrolyte of 1mol/L LiPF /EC+DMC (1:1 in mass) was tested; the electrochemical influence of 6 5wt% flame-retardant additive for the graphite / LiCoO cells (18650) was researched. 2 The results show that three flame-retardant all have good flame-retardant effects and the flame-retardant ability of Tripheyl phosphate (TPP) is best, while the electrochemical influence for the graphite / LiCoO2 cells (18650) of TCEP is least. So considering all factors, TCEP is an relatively good flame-retardant additive. Keywords: flame-retardant additive; Tri( β-chloroemethyl) phosphate (TCEP); Tripheyl phosphate (TPP); Trieresyl phosphate (TCP) 收稿日期：2006-8-22 作者简介：唐致远， （1946-），安徽人，教授，博士生导师, 主要研究方向为化学电源。E-mail ：zytang@tju.edu.cn 国家自然科学基金资助项目） 锂离子电池与其他可充电池相比具有能量密度大、工作电压高、循环寿命长、自放电率 低等优点。目前，小容量锂离子电池已成功应用于手机、数码相机、笔记本电脑等。同时， 大容量高功率锂离子动力电池也具有很好的应用前景，如将其作为电动车的动力电源可以提 供更大的动力与更长的行程，因此，大容量锂离子电池的研究引起了科学工作者的关注。大 容量锂离子动力电池商业化的主要障碍就是安全性问题，尤其是在滥用状态下（如热冲击、 过充、过放、短路等），电池往往存在着火、爆炸等安全隐患。因此如何提高锂离子电池的安 全性能成为一个迫在眉睫的问题[1-5] 。本文研究了