T型分子筛的制备研究.pdfVIP

T 型分子筛的制备 周荣飞， 林晓， 徐南平* （南京工业大学膜科学技术研究所，江苏省化学工程与技术重点实验室，南京，210009 ） 摘 要：本文就合成高结晶度的T 型分子筛进行了比较详细的研究。研究结果表明，初始硅铝溶胶摩尔组 成SiO :AlO :(Na O+K O):H O:TMAOH=1:0.055:0.31:11.67:0.045、Na O:K O= 3，控制温度在100℃，反应 2 2 3 2 2 2 2 2 2 天得到高结晶度的T 型分子筛。T 型分子筛的结晶曲线呈sigmoid 形，且结晶度受硅铝比和硅碱比的影 响很大。 关键词：T 型分子筛; 毛沸石; 菱钾沸石; 水热合成; 模板剂 Preparation of Zeolite T ZHOU Rongfei, LIN Xiao and XU Nanping （Membrane Science and Technology Research Center, Nanjing University of Technology; Key Laboratory of Chemical Engineering and Technology of Jiangsu Province, Nanjing 210009, China ） Abstract In this paper, synthesis of zeolite T with high crystallinity was studied in detail. The results indicated that the well crystallized zeolite T was synthesized with molar composition of SiO :Al O :(Na O+K O):H O:TMAOH=1:0.055:0.31:20:0.04、Na O:K O= 3 at 100℃ for 2 days. 2 2 3 2 2 2 2 2 The crystallization curves of zeolite T showed the sigmoid shape, and the crystallinity was strongly affected by Si/Al ratios and Si/alkali ratios in the gel. Keyword Zeolite T, Erionite,Offretite, Hydrothermal synthesis,Template 1 前言 T 型分子筛是菱钾沸石（offretite ）和毛沸石（erionite ）的共晶体，其硅铝比为3-4 。毛沸 石有垂直于c 轴的一维八元环的孔道，其孔道尺寸大小为0.36nm×0.51nm；而菱钾沸石有二维 * 通讯联系人：徐南平Tel.: 025 Fax: 025 Email: npxu@njut.edu.cn 基金项目：国家基础研究计划(No. 2003CB615702)，国家自然科学基金(NNSFC, No., 国家863 计 划（No. 2003AA328010 ） 1 的规则孔道，平行于c 轴的主孔道孔径为0.67nm×0.68nm，另一副孔道垂直于c 轴方向，孔径 为0.36nm×0.49nm。 水热法合成分子筛可以分为均相和非均相两种体系。均相体系又称为清液，加入的原料完 全溶解成透明状，适宜合成铝含量低的分子筛，如ZSM-5 、丝光沸石和P 、Y