改性木质素磺酸盐水煤浆添加剂对神华煤制浆性能的影响研究.pdfVIP

全国第十三次工业表面活性剂研究与开发会议 改性木质素磺酸盐水煤浆添加剂对神华煤制浆性能的影响* 张群彩 杨东杰 欧阳新平 邱学青** (华南理工大学 化工与能源学院 广东广州 510 640) 摘 要: 针对神华煤难以制成高浓度水煤浆的现状 采用 Haake RV 流变仪等研究了改性木质素磺酸盐水煤 浆添加剂(GCL3S)对神华煤水煤浆制浆性能的影响 GCL3S 的质量分数为 0.8 制得的煤浆中煤质量分数达到 62.63 黏度可低至 896 mPa.s 优于同等条件下萘系添加剂 FDN 的降黏效果 在接近中性条件下 GCL3S 的 制浆性能最好 升高温度可以提高浆中煤的质量分数, 对于用GCL3S 制得的浆体 最佳搅拌时间是20min 40min 其抗剪切性能明显优于FDN, GCL3S 对煤浆的稳定时间为10d 优于萘系添加剂 关键字 水煤浆 神华煤 木质素磺酸钠 Abstract: Since Shenhua Coal is difficult to prepare the high concentration slurry, the modified sodium lignosulphonate (GCL3S) was used as dispersant of coal water slurry (CWS). The aim of this investigation is to determine the effect of GCL3S on the properties of CWS by means of the rheometer. The effects of dispersant concentration, temperature and pH on the flow characteristics of CWS were investigated systematically. The results show that the lowest viscosity of 896 mPa.s and excellent fluidity of the slurry can be obtained using GCL3S at the concentration of 0.8% and the concentration of coal is 62.63%. Which is more excellent than that of the naphthalene sulfonate-formaldehyde condensate (FDN). The pH is approaching 7.0, and the suitable stirring time is 20 min 40 min in the process of preparation of CWS, and the higher temperature can increase the coal concentration. Keywords : coal water slurry ; Shenhua coal; lignosulfonates ; Foundation item Supported by the Science and Technology Programme of Guangdong Province of China 自从爆发第一次石油危机以来 以煤代油是当今普遍关注的一个重要课题,水煤浆(CWS)是由60 75 的煤 25 40 的水和大约 1 的化学添加剂组成 由于水煤浆既能保持煤的物理化学 性能,又能像石油一样具有良好的流动性和稳定性 具有代油 节能 环保等多种效益,成为煤炭加 工利用的一项重要技术[1] 神华集团是我国最大的煤炭生产商 2005 年计划产煤 1.5 亿吨 为世界第三 但由于神华煤 [2] 的内在水含量和氧含量过高 难