热疲劳测试对热作模具钢残留应力之影响.PDFVIP

120 (2014) 4 1-46 Thermal Fatigue Effect on the Residual Stress of Hot Work Steel 1 1* 1 1 2 3 Y.W. Yeh L.H. Chiu C.Y. Yang Y.Y. Su Y.J. Yeh H. Yataka Received 1 January 2014; received in revised form 15 February 2014; accepted 20 March 2014 摘　要 Abstract JI S SKD 6 1 Thermal fatigue cracking is one of the most important failure mechanisms in hot work die steels. This study investigates thermal fatigue effect on the residual stress of hot work steel. A novel method using induction heating DAC 47 equipment was employed to investigate the HRC 400 kHz 30 kW thermal fatigue behaviors of hot-work steel, 2.5 2 SKD 61 (DAC), vacuum hardened treated to 47 500-4000 100 HRC. Microstructure, X-ray diffraction and thermal fatigue tests were conducted. Residual stress were calculated by on cos method de- veloped by PULSTEC company using on X-ray X -ray cos devices. The results show that tensile stress existed in the rolled direction and compressive stress existed in the radial direction of speci- men. The compressive stress of -340 MPa was -340 MPa 500 existed quench and temper specimen. The re- -