少渣冶炼再循环炉渣熔化特性及其应用效果的研究北京金属学会.docVIP

脱碳炉返回用渣熔化特性及其应用效果的研究 吴 伟， 孟 华 栋， 刘 浏 （钢铁研究总院冶金工艺研究所 北京 100081） 摘 要：为了充分利用脱碳炉炉渣对其进行轻打水和焖渣处理，之后作为脱磷炉的炉料。本文主要研究了轻打水和焖渣处理后炉渣的熔化特性以及在脱磷炉作为炉料的应用效果。结果表明，从化学成分和岩相分析上看，焖渣的水分高于干渣，两者的全铁含量都较高，熔点相近；干渣中硅酸二钙含量高于焖渣的，而硅酸三钙含量低于焖渣的，两者都含有一定量的铁酸钙，有利于脱磷和化渣。从应用的效果看，通过每炉次加入3~6吨的干渣或焖渣，每炉可节省石灰0.7~1吨，终点成分控制达到了要求。加入干渣和焖渣的脱磷炉终点炉渣的岩相组成主要是硅酸二钙、RO相和玻璃相，与不加返回渣得到的脱磷炉终渣成分的相差不大，使用干渣的终渣中含有少量的铁酸钙有利于脱磷。由此表明，采用干渣和焖渣都能达到一定的脱磷效果。 关键词：脱碳炉；返回用渣；熔化特性；脱磷炉；冶金效果 The Melting Characteristics of the Recycling Slag in Decarburization Converter and its Application Effects WU Wei, MENG Hua-dong, LIU Liu (Metallurgical Technology Research Department of Central Iron Steel Research Institute, Beijing 100081) Abstract: The steel slag in the decarburization converter is treated by little water-spreading and heat-stewed methods, which is used as the furnace burden of the dephosphorization converter. The slag characteristics by little water-spreading and heat-stewed methods and its application effects as the furnace burden are researched. The results show the water content in heat-stewed slag is higher than that of little water-spreading slag. There is higher total iron content in heat-stewed and little water-spreading slag and almost same melting point. The dicalcium silicate content in little water-spreading slag is higher than that in heat-stewed slag. The tricalcium silicate in little water-spreading slag is lower than that in heat-stewed slag. There are a lot of calcium ferrite in little water-spreading and heat-stewed slag, which is beneficial to dephosphorization and slag melting. The little water-spreading and heat-stewed slag are added to dephosphorization converter each charge by 3 or 6 tons. The results show that the saving lime is 0.7~1 tons each charge. The petrographic constitute of final slag for the dephosphorization converter by adding the little water-spreading and heat-stewed slag is dicalcium silicate, RO phase and glass phase. There are little calcium ferrite phase in the little water-spreading