gc1030硬质合金--加工模具用高效长寿命切削刀具材料（Gc1030 cemented carbide -- high efficiency and long life cutting tool material for machining dies）.doc

gc1030硬质合金--加工模具用高效长寿命切削刀具材料（Gc1030 cemented carbide -- high efficiency and long life cutting tool material for machining dies） The new GC1030 hard alloy Sandvik is worlds first developed TiAlN super multi coated carbide tool materials, it is in the process of mould material, play a superior performance to improve the machining efficiency and prolong tool life. (1) the problems caused by the change of mould material In recent years, with the continuous improvement of the performance of the mold material, the life of the mold is extended, but the machinability of the mold material (cutting and grinding) is also getting worse. In recent years, great changes have taken place in the mold processing method, the traditional processing methods are machined from machining, quenching, fine transition to direct machining of hardened materials, thereby reducing the manufacturing process, reduce processing costs. For SKD61 direct machining of hardened materials, does not appear too big; but for the cross century new mold material developed in recent years, not only can improve the cutting conditions, it is difficult to ensure the tool life. This is a big problem that can not be ignored. (2) the cause of deterioration of machinability At present, corresponding to various different purpose, properties of die materials were optimized, the common pursuit of the performance is excellent with high hardness, high toughness, high corrosion resistance, the machined surface is smooth and beautiful, quality. In order to meet the requirements of these characteristics, it is necessary to add various alloying elements, control the crystallization structure of materials, remove impurities and other measures. However, from the angle of cutting tool to look at these performance improvements, you will find that it brings to the tool cutting resistance than rise, tip damage increases the risk, easy cutting and other problems caused by bond components decrease. In order to solve these problems, i