直接淬火技术应用于超高强度低合金耐磨钢板之开发.PDFVIP

直接淬火技術應用於超高強度低合金耐磨 鋼板之開發 Development of a Direct-Quenching and Self-Tempering Process for Producing Abrasion Resistant Steel Plate 1 2 1 3 4 D. Chen, Y.T. Wang, W.C. Chung, L.C. Ping, E. Lo Conventional abrasion resistant steel plates are produced by reheating-quenching tempering process (RQ-T). RQT process produces the steel plates with desir ed micr ostru ctur e an d m ech anical pr op erties thr ou gh op t im al contr ol of th e r e -au st en iz at i on temperature, cooling rate, and tempering parameters. (Direct quenching) In this study, we developed direct-quenching and self- tempering processes to produce an abrasion resistant - steel plate, PA500H . With proper alloy design , the (Direct-Quenching Self-Tempering, martensite formed during the quenching process was DQST) auto-tempered by the heat dissipated from the center of DQST the plate. We used a quenching-deformation dilatometer to simulate the auto-tempering behavior of martensite microstructures of different cooling patterns and finish cooling t emp er atur es (FCTs) . Th e micr ostru ctur e DQST PA500H simulation provided useful information for producing 1170MPa PA500H in the plate mill. The PA500H had a yield 1760MPa 15% strength 1,170 MPa, a tensile strength 1,760 MPa, and 510HBW -40L an elongation rate 15%. The hardness of the PA500H 40J exceeded 500HBW and longitudinal Charpy absorption DQST energy at -40also reached 40J. Our test results showed that the DQST process was well-suited for producing abrasion resist