n镀膜转速及无电镀镍对铜合金化延性铸铁摩擦行为之影响.pdfVIP

112 (2012) 55-61 CAD-(Cr,Zr)N Effect of CAD Rotation Rate of CrN/ZrN/EN Coatings on Friction Behavior of Copper Alloyed Ductile Iron 1* 1 2 3 Y.C. Pan S.C. Kung C.H. Hsu Y.X. Hu Received 1 January 2012; received in revised form 23 February 2012; accepted 29 February 2012 Abstract 1 wt% This study utilized electroless nickel (EN) (EN) and cathodic arc deposition (CAD) technologies (1~4 rpm) to treat the 1wt% Cu alloyed ductile iron (CAD) CrN/ZrN substrates. First, EN was used as an interlayer, CAD and then CrN/ZrN coatings were deposited by using a CAD method. Further, the effect of EN CAD-CrN/ZrN rotation rate for CrZrN/EN duplex coatings on SEM XRD TEM wear behavior of the iron was investigated. Ball-on-disc Coating morphology and structure were analyzed by using SEM, XRD, and TEM. EN Moreover, nanoindention test and wear test CrZrN F.C.C CrN/ZrN were both performed for understanding wear 2 rpm EN/CrN/ behavior of copper alloyed ductile iron. The ZrN EN CAD-CrN/ results showed that EN was an amorphous ZrN (HF1) structure while the CrN/ZrN film was a (31.1 GPa) (256.4 GPa) multilayer type with a FCC structure.