Hans Journal of Civil Engineering 土木工程, 2017, 6(6), 557-563 Published Online November 2017 in Hans. /journal/hjce /10.12677/hjce.2017.66067 Study on Preparation and Properties of Desulfurized Rubber Modified Asphalt Qingpeng He, Huiqiang Chen, Yuanren Fang, Dalu Liu, Jianbang Sun School of Civil Engineering, Chongqing Jiaotong University, Chongqing th th nd Received: Oct. 13 , 2017; accepted: Oct. 28 , 2017; published: Nov. 2 , 2017 Abstract In this paper, the desulfurization rubber powder is used to prepare the desulfurization rubber as- phalt; the optimum dosage, reasonable particle size and asphalt modification process are deter- mined. By contrast test, the road performance of desulfurized rubber asphalt and ordinary rubber asphalt is systematically studied. The results show that the optimum dosage of desulfurized rubber asphalt is 18%, and the desulfurization powder with 30 meshes is the best. The preparation process is shear rate 5000 r/min, shear temperature 160˚C - 170˚C, shear time 45 min, developed at 160˚C for 45 min. Compared with ordinary rubber asphalt, the viscosity of desulfurized rubber asphalt de- creased; storage stability, anti-aging performance, low temperature performance were significantly improved, but the high temperature performance was slightly inadequate. Keywords Desulfurization Powder, Modified Asphalt, Preparation Process, Road Performance 脱硫橡胶改性沥青的制备与性能研究 何青蓬，陈辉强，方源仁，刘大路，孙建邦 重庆交通大学土木工程学院，重庆 收稿日期：2017年10月13 日；录用日期：2017年10月28 日；发布日期：2017年11月2 日 摘 要 本文采用脱硫胶粉制备脱硫橡胶沥青，确定胶粉的最佳掺量、合理粒径及沥青改性的制备工艺，通过对 比试验，系统研究脱硫橡胶沥青与普通橡胶沥青的路用性能。结果表明，脱硫橡胶沥青最佳掺量为18%， 文章引用: 何青蓬, 陈辉强, 方源仁, 刘大路, 孙建邦. 脱硫橡胶改性沥青的制备与性能研究[J]. 土木工程, 2017, 6(6): 557-563. DOI: 10.12677/hjce